The internal structure of nanometric microgels in water has been studied as a function of temperature, crosslinker content, and level of deuteration. Small-angle neutron scattering from poly(N-isopropylmethacrylamide) (pNIPMAM, volume phase transition ≈ 44 °C) microgel particles of radius well below 100 nm in D2O has been measured. The intensities have been analyzed with a combination of polymer chain scattering and form-free radial monomer volume fraction profiles defined over spherical shells, taking polydispersity in size of the particles determined by AFM into account. A reverse Monte Carlo optimization using a limited number of parameters was developed to obtain smoothly decaying profiles in agreement with the experimentally scattered intensities. Result are compared to the swelling curve of microgel particles in the temperature range from 15 to 55 °C obtained from photon correlation spectroscopy (PCS). In addition to hydrodynamic radii measured by PCS, our analysis provides direct information about internal water content and gradients, the strongly varying steepness of the density profile at the particle-water interface, the total spatial extension of the particles, and the visibility of chains. The model has also been applied to a variation of the crosslinker content, N,N′-methylenebisacrylamide (BIS), from 5 to 15 mol%, providing insight in the impact of chain architecture and crosslinking on water uptake and on the definition of the polymer-water interface. The model can easily be generalized to arbitrary monomer contents and types, in particular mixtures of hydrogenated and deuterated species, paving the way to detailed studies of monomer distributions inside more complex microgels, in particular core-shell particles.

We study the swelling and shrinking behavior of core-shell microgels adsorbed on silicon wafers. In these systems, the core is made of cross-linked poly(N-isopropylmethacrylamide) and the shell consists of cross-linked poly(N-n-propylacrylamide). In suspension, these particles exhibit an extended linear swelling behavior in the temperature interval between the lower critical solution temperatures of the two polymers. Using ellipsometry and atomic force microscopy, we show that this linear response is also observed in the adsorbed state.

The effect of deuteration on the volume phase transition (VPT) temperature of poly (N-isopropylmethacrylamide) (pNIPMAM) microgels in aqueous suspension is determined via IR spectroscopy and size measurements by photon correlation spectroscopy (PCS). We study the effect of a hydrogenated and a deuterated solvent (H2O/D2O), and of the hydrogenated and (partially) deuterated monomer. Deuteration of the monomer or copolymerization with deuterated monomers shifts the volume phase transition temperature (VPTT) by up to 8.4 K to higher temperatures, in good agreement with known results for pNIPAM microgels. Moreover, the shape of the swelling curve is found to depend on deuteration, with the highest deuteration leading to the sharpest VPT. Finally, the quantitative agreement between FTIR spectroscopy and PCS evidences the spatial homogeneity of the microgel particles. Our results are rationalized in terms of the effect of deuteration on hydrogen bonding. They shall be of primary importance for any experimental measurements close to the VPT involving isotopic substitution, and in particular contrast variation small angle neutron scattering.

The structural basis for linear thermoresponses of smart core–shell microgels is elucidated by FTIR spectroscopy, being sensitive to core processes.

The peculiar linear temperature-dependent swelling of core-shell microgels has been conjectured to be linked to the core-shell architecture combining materials of different transition temperatures. Here the structure of pNIPMAM-core and pNNPAM-shell microgels in water is studied as a function of temperature using small-angle neutron scattering with selective deuteration. Photon correlation spectroscopy is used to scrutinize the swelling behaviour of the colloidal particles and reveals linear swelling. Moreover, these experiments are also employed to check the influence of deuteration on swelling. Using a form-free multi-shell reverse Monte Carlo approach, the small-angle scattering data are converted into radial monomer density profiles. The comparison of ‘core-only’ particles consisting of identical cores to fully hydrogenated core-shell microgels, and finally to H-core/D-shell architectures unambiguously shows that core and shell monomers display gradient profiles with strong interpenetration, leading to cores embedded in shells which are bigger than their isolated ‘core-only’ precursor particles. This surprising result is further generalized to different core cross-linker contents, for temperature ranges encompassing both transitions. Our analysis demonstrates that the internal structure of pNIPMAM-core and pNNPAM-shell microgels is heterogeneous and strongly interpenetrated, presumably allowing only progressive core swelling at temperatures intermediate to both transition temperatures, thus promoting linear swelling behaviour.

The radial density profile of deuterated poly(N,n-propyl acrylamide) shell monomers within core–shell microgels has been studied by small-angle neutron scattering in order to shed light on the origin of their linear thermally-induced swelling.