No abstract

This article deals with the preparation and characterization of silk fibroin(Bombyz mori)/ cellulose blend films. Following dissolution with a metal complex solution, the average .molecular weight of silk fibroin slightly decreased, while cellulose was almost unaffected. After coagulation and washing, transparent films were obtained by blending fibroin and cellulose in all proportions. The crystalline structures of regenerated fibroin and cellulose were &form and cellulose 11, respectively, as shown by the characteristic x-ray diffraction profiles. Density values increased with cellulose content, though less than expected from a pure additive behavior. Moisture regain increased following the addition of a small amount of cellulose to silk fibroin. The mechanical properties showed that both strength and elongation at break of silk fibroin films were improved by blending with cellulose. IR spectra exhibited changes in the skeletaI frequences of silk fibroin, suggesting the occurrence of intermolecular interactions between fibroin and cellulose through hydrogen bond formation.

No abstract

This research concerns the development of a SF 6 RF discharge at low pressure in a small reactor for industrial applications. The plasma is produced in the pressure range 0.05-1 mbar by a RF supply. The pumping system sustains a flowrate of about 50 cm s −1 , with residence time in the discharge of about 0.2 s at a pressure of 0.1 mbar. The discharge parameters were measured at a low operation power. Measurements were performed by means of movable electrostatic probes and a photodiode. Particular care in the analysis of the data proved to be necessary due to the presence of a substantial amount of negative ions. The reactor has been employed for textile treatment in order to modify the surface properties of the fibres. Favourable operating conditions leading to an improved hydrophobicity of the textiles were achieved.

Poly(ethylene terephthalate) (PET) and cotton fibres, treated in an appositely set up RF SF 6 plasma reactor under different operating conditions, were characterised by XPS, EPR, DSC, XRD, ATR analyses, water contact angle and water droplet roll-off angle measurements. The ageing of plasma-treated samples was also investigated under different post-treatment conditions. Plasma treatment led to efficient implantation of fluorine atoms on the surface of both polymers; this resulted in water repellence without altering the bulk properties of the polymers. The radical species formed in the plasma-activated polymer surface were involved in its fluorination and in the subsequent uptake of atmospheric oxygen. Surface reorganisation of polymer segments, tending to reduce the interfacial energy between the polymer and the phase in contact with it, induced the surface modifications observed under ageing and in samples plasma-treated several times. An increase in the depth of the fluorinated layer, leading to outstanding stable hydrorepellence, was achieved by repeated SF 6 plasma treatments, followed by surface rearrangements favoured by swelling.