Natural zeolites are low in cost and exhibit interesting properties for applications in adsorption and catalysis. However, the fact that they are natural materials, not obtained in pure form, and can incorporate various compensating ions can compromise their properties and restrict their use. As their textural and chemical properties are of great relevance for adsorption and catalysis applications, this work aims to study the modification of the natural zeolite clinoptilolite to obtain materials with better physicochemical properties. Clinoptilolite was treated with NaOH under various conditions. The treated material was characterized by X-ray diffraction, X-ray fluorescence, N2 adsorption and desorption at 77 K, CO2 adsorption at 273 K, and pyridine adsorption. The treatment allowed the removal of silicon from the material, improving the textural properties and preserving the structural Al. With the removal of Si, the Si/Al ratio decreased, and consequently, the number of acid and adsorptive sites increased. In addition, statistical planning revealed that the concentration of NaOH is the parameter that most influences the improvement of the textural properties.
In this study, blends based on a high density polyethylene (HDPE) and chitosan (CS) were successfully prepared by melt processing, in a laboratory internal mixer. The CS biopolymer content effect (up to maximum of 40%), and, the addition of bentonite clay modified with quaternary ammonium salt (CTAB) impregnated chitosan as a compatibilizing agent, on the properties of the blends was analyzed by Fourier transform-infrared spectroscopy (FT-IR), wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), thermogravimetric analyses (TG), tensile strength, and scanning electron microscopy (SEM). The use of clay modified with CTAB impregnated chitosan, employing a method developed here, improved the compatibility of HDPE with chitosan, and therefore the thermal and some of the mechanical properties were enhanced, making HDPE/chitosan blends suitable candidates for food packaging. It was possible to obtain products of synthetic polymer, HDPE, with natural polymer, chitosan, using a method very used industrially, with acceptable and more friendly properties to the environment, when compared to conventional synthetic polymers. In addition, due to the possibility of impregnated chitosan with quaternary ammonium salt exhibit higher antibacterial activity than neat chitosan, the HDPE/chitosan/organobentonite blends may be potentially applied in food containers to favor the preservation of food for a longer time in comparison to conventional materials.
In this study, an antimicrobial packaging material was successfully developed with blends of high-density polyethylene (HDPE) and chitosan (CS) made by melt processing. In the different HDPE/CS composites, the CS content effect (up to 40%), and the addition of quaternary ammonium salt functionalized chitosan (CS-CTAB) as an additive were evaluated by X-ray diffraction (XRD), differential scanning calorimetry (DSC), thermogravimetric analyses (TG), tensile strength, scanning electron microscopy (SEM) and antimicrobial activity. When analyzing the effect of the additive in the different HDPE/CS composites, it was observed that the compositions with 10 and 20 %wt of chitosan showed better elongation values (~13% and 10%) as well as a higher decomposition temperature at 20% mass loss (T20) varying from (321–332 °C and 302–312 °C), respectively, in relation to the other compositions, regardless of the type of additive used, it acted as an antimicrobial agent, promoting inhibition of microbial growth against the strains gram-positive and gram-negative used in this work, making the different HDPE/CS composites suitable candidates for use in food packaging.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.