The purpose of this study is to evaluate the effects of aging by thermocycling on the mechanical and tribological properties of two indirect filling commercial resin-based restorative composite materials. The studied composites are referenced by the capital letters: A and B. The commercial trade names are omitted, to avoid commercial references. Forty specimens of each material were produced and divided into three groups: a control group not subjected to aging, and two groups, T 1 and T 2 submitted to different thermocycling conditions. The studied properties were surface roughness, elastic modulus (determined dynamically by impulse excitation of vibration, and statically by four-point bending test), flexural strength and work of fracture (four-point bending test), micro-hardness (Vickers micro-indentation) and coefficient of friction (scratch test). From this study, it was possible to conclude that Composite A, in addition to having better mechanical properties, is less affected by thermocycling than Composite B, which suggests that it will better withstand the stresses, both mechanical and thermal, which it is subjected to. It is also possible to infer that the thermocycling regimen proposed by Standard ISO 11405 (Dental materialstesting of adhesion to tooth structure, 2003) is not sufficient to adequately simulate the degradation caused by the oral Technical Editor: Estevam Las Casas.
RESUMO:A madeira laminada colada (MLC) é produzida a partir da colagem de peças de madeira. No Brasil, o emprego da madeira de espécies nativas para produzir elementos estruturais de MLC não ocorre em condições tecnológicas satisfatórias, sendo dificultado por não serem totalmente conhecidas as suas propriedades e seu desempenho em diferentes condições de serviço. Neste estudo, objetivou-se determinar e relacionar o módulo de elasticidade dinâmico (E Mvt ) com o módulo de elasticidade estático (E M ), o módulo de ruptura (f M ), a resistência à compressão (σ cp ) e o módulo de elasticidade paralelo (E cp ), e avaliar o desempenho da espécie nativa Cedrinho (Erisma uncinatum Warm.) na construção de vigas de MLC. As vigas de MLC foram produzidas com peças de madeira classificadas, coladas por adesivos à base de resorcina fenol formaldeído (RFF) e poliuretano (PUR), com intensidades de pressão de 0,8 MPa e 1,2 MPa e distribuições aleatórias e não aleatórias das lâminas. A avaliação dessas vigas de MLC também foi realizada por meio de corpos de prova de compressão paralela às linhas de cola e de delaminação. Verificou-se que o E Mvt obtido por meio de ensaios dinâmicos de vibração transversal apresentou um coeficiente de correlação com o E M obtido no ensaio de flexão estática (R 2 = 0,86) e significativo ao nível de 1% de probabilidade (P < 0,01). Dessa forma, pode-se concluir que o E Mvt é um bom estimador do E M . Constatou-se que essa espécie de madeira pode ser utilizada em MLC e encontra-se na classe de resistência C30 das folhosas.Palavras-chave: Vibração transversal, vigas de MLC, madeira tropical, ensaios não destrutivos. EVALUATION OF GLUED LAMINATED TIMBER BEAMS OF CEDRINHO(Erisma uncinatum Warm.) ABSTRACT: Glued laminated timber (glulam) is assembled layers of bonded pieces of timber. In Brazil, the use of native species timber to produce structural elements of glulam does not occur in satisfactory technological conditions. This is because the properties and performance of native species of wood, under various service conditions, are not entirely known. This study aims at determining and to relate the dynamic modulus of elasticity (E Mvt ) and the static modulus of elasticity (E M ), the modulus of rupture (f M ), the compression parallel strength (σ cp ) and the parallel elastic modulus (E cp)
ABSTRACT. The grading of structural lumber besides contributing for increasing the structure's safety, due to the reduction of the material variability, also allows its rational use. Due to the good correlation between strength and bending stiffness, the latter has been used in estimating the mechanical strength of lumber pieces since the 60's. For industrial application, there are equipment and techniques to evaluate the bending stiffness of lumber, through dynamic tests such as the longitudinal vibration technique, also known as stress wave, and the transverse vibration technique. This study investigated the application of these two techniques in the assessment of the modulus of elasticity in bending of Teca beams (Tectona grandis), from reforestation, and of the tropical species Guajará (Micropholis venulosa). The modulus of elasticity estimated by dynamic tests showed good correlation with the modulus measured in the static bending test. Meantime, we observed that the accuracy of the longitudinal vibration technique was significantly reduced in the evaluation of the bending stiffness of Teca pieces due to the knots existing in this species.Keywords: lumber, non-destructive evaluation, dynamic tests.Avaliação da rigidez à flexão de peças estruturais de Teca e Guajará pelos ensaios de vibração transversal e vibração longitudinal RESUMO. A classificação de peças estruturais de madeira, além de contribuir para aumentar a segurança das estruturas, em função da redução da variabilidade do material, permite também a utilização racional desse material. Pela boa correlação entre resistência mecânica e rigidez à flexão, essa última tem sido empregada na estimativa da resistência mecânica de peças de madeira serrada desde a década de 60. Para a aplicação industrial, existem equipamentos e técnicas que permitem avaliar a rigidez à flexão da madeira serrada, por meio de ensaios dinâmicos como, por exemplo, a técnica de vibração longitudinal, também conhecida como ondas de tensão e a técnica de vibração transversal. O objetivo deste trabalho foi investigar a aplicação dessas duas técnicas na avaliação do módulo de elasticidade à flexão de vigas da espécie Teca (Tectona grandis), proveniente de reflorestamento, e da espécie tropical Guajará (Micropholis venulosa). O módulo de elasticidade estimado com os ensaios dinâmicos mostrou boa correlação com o módulo de elasticidade medido no ensaio estático de flexão. Entretanto, observou-se que a exatidão da técnica de vibração longitudinal foi reduzida significativamente na avaliação da rigidez a flexão das peças Teca em função dos nós existentes nessa espécie.Palavras-chave: madeira serrada, avaliação não-destrutiva, ensaios dinâmicos.
This paper presents an experimental analysis of the pullout strength of bonded and axially loaded steel rods used as connector elements in log-concrete composite bridge decks. Static and cyclic tests were carried out to evaluate the fatigue of the connectors using two species of reforested wood, three types of commercial adhesives and three levels of wood moisture content. It was found that six failure modes (rod interface failure, timber interface failure, combined timber interface/rod interface failure, combined rod interface/timber substrate failure, rod failure, and adhesive failure) can occur in the geometry of a single test specimen. The results indicate the good performance of epoxy glued steel rod connectors for use in log-concrete composite bridge decks.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.