Due to the low mechanical performances of 3D-printed denture base resins, ZrO2 nanoparticles (ZrO2NPs) were incorporated into different 3D-printed resins and their effects on the flexure strength, elastic modulus, impact strength, hardness, and surface roughness were evaluated. A total of 286 specimens were fabricated in dimensions per respective test and divided according to materials into three groups: heat-polymerized as a control group and two 3D-printed resins (NextDent and ASIGA) which were modified with 0.5 wt.%, 1 wt.%, 3 wt.%, and 5 wt.% ZrO2NPs. The flexure strength and elastic modulus, impact strength, hardness, and surface roughness (µm) were measured using the three-point bending test, Charpy’s impact test, Vickers hardness test, and a profilometer, respectively. The data were analyzed by ANOVA and Tukey’s post hoc test (α = 0.05). The results showed that, in comparison to heat-polymerized resin, the unmodified 3D-printed resins showed a significant decrease in all tested properties (p < 0.001) except surface roughness (p = 0.11). In between 3D-printed resins, the addition of ZrO2NPs to 3D-printed resins showed a significant increase in flexure strength, impact strength, and hardness (p < 0.05) while showing no significant differences in surface roughness and elastic modulus (p > 0.05). Our study demonstrated that the unmodified 3D-printed resins showed inferior mechanical behavior when compared with heat-polymerized acrylic resin while the addition of ZrO2NPs improved the properties of 3D-printed resins. Therefore, the introduced 3D-printable nanocomposite denture-base resins are suitable for clinical use.

This study investigated the translucency of 3D-printed denture base resins modified with zirconium dioxide nanoparticles (ZrO2NPs) under thermal cycling. A total of 110 specimens were fabricated and divided into 3 groups according to the materials, i.e., heat-polymerized resin, and 3D-printed resins (NextDent, and ASIGA). The 3D-printed resins were modified with 0, 0.5, 1, 3, and 5 wt.% of ZrO2NPs. All the specimens were subjected to 5000 thermal cycles. The translucency was measured using a spectrophotometer. The results showed that the heat-polymerized resin had considerably higher translucency than the 3D-printed resins. Compared to the unmodified group, the translucency decreased significantly after adding 5% ZrO2NPs to NextDent and 3% ZrO2NPs to ASIGA resins. The highest translucency was achieved for NextDent by adding 0.5% ZrO2NPs and for ASIGA without any ZrO2NPs. It was found that the average concentration level in ASIGA was significantly higher than that in NextDent. These findings revealed that 3D-printed resins have lower translucency than heat-polymerized acrylic resin, and adding ZrO2NPs at low concentrations did not affect the translucency of the 3D-printed resins. Therefore, in terms of translucency, 3D-printed nanocomposite denture base resins could be considered for clinical applications when ZrO2NPs are added at low concentrations.