Self-standing films (45-μm thick) of native cellulose nanofibrils (CNF) were synthesized and characterized for their piezoelectric response. The surface and the microstructure of the films were evaluated with image-based analysis and scanning electron microscopy (SEM). The measured dielectric properties of the films at 1 kHz and 9.97 GHz indicated a relative permittivity of 3.47 and 3.38 and loss tangent tan of 0.011 and 0.071, respectively. The films were used as functional sensing layers in piezoelectric sensors with corresponding sensitivities of 4.7 to 6.4 pC/N in ambient conditions. This piezoelectric response is expected to increase remarkably upon film polarization resulting from the alignment of the cellulose crystalline regions in the film. The CNF sensor characteristics were compared with those of polyvinylidene fluoride (PVDF) as reference piezoelectric polymer. Overall, the results suggest that CNF is a suitable precursor material for disposable piezoelectric sensors, actuator or energy generators with potential applications in the fields of electronics, sensors and biomedical diagnostics.
Block copolymers of poly(2-(dimethylamino)ethyl methacrylate) (PDMAEMA) and poly(oligo(ethylene glycol) methyl ether methacrylate) (POEGMA) with varying block sizes were synthesized by consecutive reversible addition-fragmentation chain transfer (RAFT) polymerization and then exposed to cellulose substrates with different anionic charge density. The extent and dynamics of quaternized PDMAEMA-b-POEGMA adsorption on regenerated cellulose, cellulose nanofibrils (CNF), and (2,2,6,6-tetramethylpiperidin-1-yl)oxyl (TEMPO)-oxidized cellulose nanofibrils (TOCNF) was determined by using electromechanical and optical techniques, namely, quartz crystal microbalance (QCM-D) and surface plasmon resonance (SPR), respectively. PDMAEMA-b-POEGMA equilibrium adsorption increased with the anionic charge of cellulose, an indication of electrostatic interactions. Such an observation was further confirmed by atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). Depending on their architecture, adsorption on TOCNF of some of the PDMAEMA-b-POEGMA copolymers produced a significant reduction in QCM frequency, as expected from large mass uptake, while surprisingly, other copolymers induced the opposite effect. This latter, remarkable behavior was ascribed to coupled water expulsion from the interface upon charge neutralization of anionic surface sites with adsorbing cationic polymer segments. These observations were further investigated with SPR and QCM-D measurements using deuterium oxide solvent exchange to determine the amount of coupled water at the TOCNF-block copolymer interface. Finally, random copolymers with similar composition adsorbed to a larger extent compared to the respective block copolymers, revealing the effect of adsorbed loops and tails as well as hydration.
We demonstrate benzophenone (BP) conjugation via amine-reactive esters onto oxidized cellulosic fibers that were used as precursors, after microfluidization, of photoactive cellulose nanofibrils (CNF). From these fibrils, cellulose I filaments were synthesized by hydrogel spinning in an antisolvent followed by fast biradical UV cross-linking. As a result, the wet BP-CNF filaments retained extensively the original dry strength (a remarkable ∼80% retention). Thus, the principal limitation of these emerging materials was overcome (the wet tensile strength is typically <0.5% of the value measured in dry conditions). Subsequently, antihuman hemoglobin (anti-Hb) antibodies were conjugated onto residual surface carboxyl groups, making the filaments bifunctional for their active groups and properties (wet strength and bioactivity). Optical (surface plasmon resonance) and electroacoustic (quartz crystal microgravimetry) measurements conducted with the bifunctional CNF indicated effective anti-Hb conjugation (2.4 mg m), endowing an excellent sensitivity toward Hb targets (1.7 ± 0.12 mg m) and negligible nonspecific binding. Thus, the anti-Hb biointerface was deployed on filaments that captured Hb efficiently from aqueous matrices (confocal laser microscopy of FITC-labeled antibodies). Significantly, the anti-Hb biointerface was suitable for regeneration, while its sensitivity and selectivity in affinity binding can be tailored by application of blocking copolymers. The developed bifunctional filaments based on nanocellulose offer great promise in detection and affinity binding built upon 1D systems, which can be engineered into other structures for rational use of material and space.
A method for preparing photo-crosslinkable cellulose nanofibrils (CNF) was investigated.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.