In this study, the reinforcing potential of cellulose “microfibres” obtained from bleached softwood kraft pulp was demonstrated in a matrix of polyvinyl alcohol (PVA). Microfibres are defined as fibres of cellulose of 0.1–1 μm in diameter, with a corresponding minimum length of 5–50 μm. Films cast with these microfibres in PVA showed a doubling of tensile strength and a 2.5-fold increase in stiffness with 5% microfibre loading. The theoretical stiffness of a microfibre was calculated as 69 GPa. The study also demonstrated that the strength of the composite was greater at 5% microfibre loading compared to 10% loading. Comparative studies with microcrystalline cellulose showed that the minimum aspect ratio of the reinforcing agent is more criticalthan its crystallinity in providing reinforcement in the composite.
ABSTRACT:The effects of moisture, temperature, and ultraviolet (UV) light on performance of natural-fiber-plastic composites (NFPC) were assessed. We conducted short-term tests in the laboratory and long-term tests under natural exposure and measured changes in mechanical properties and color in samples of the composite. Chemical changes of the composite's materials were measured by X-ray photoelectron spectroscopy to elucidate the mechanisms of chemical transformations on the material surface. Relative humidity highly affected the modulus of rupture (MOR) and the modulus of elasticity (MOE), and had a greater effect than temperature and UV exposure on performance of the composite. The lightness of the composite was increased by the UV effect in the short-and the long-term tests. The X-ray photoelectron spectroscopy (XPS) analysis suggested that the composite was protected by the UV absorber.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.