Soft x-ray magnetic circular dichroism (XMCD) and element-specific magnetic hysteresis (ESMH) measurements were performed in transmission mode on Mn73Ir27 10nm∕Co70Fe30 2nm bilayers with different chemical orderings of the Mn–Ir layer.The unidirectional anisotropy constant was 0.55erg∕cm2 for the disordered Mn–Ir layer and 1.18erg∕cm2 for the ordered Mn–Ir layer. The XMCD signal of Mn was observed, which means the induced ferromagnetic component of Mn spins through the exchange coupling at the interface. No vertical offset of the Mn ESMH loops was observed for either the disordered or the ordered bilayers, which means that insignificant uncompensated Mn spin was pinned at the interface to induce exchange bias on the Co–Fe layer.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.