The useful life of superheaters and reheaters of power stations which use heavy fuel oil is shortened and their continuous service is inhibited by corrosion (fireside) and creep-type problems. The increase of corrosion attack on boilers is caused by the presence of fuel ash deposits containing mainly vanadium, sodium, and sulfur which form low-melting-point compounds. The tubes are exposed to the action of high stresses and high temperatures, producing the so-called "creep damage." In this work, two kinds of results are reported: lab and field studies using a 2.25Cr-1Mo steel. The laboratory work was in turn divided into two parts. In the first, the steel was exposed to the action of natural ash deposits in oxidant atmospheres at 600 °C for 24 h. In the second part, tensile specimens were creep tested in Na 2 SO 4 , V 2 O 5 , and their mixture over a temperature range of 580 to 620 °C. In the field work, components of a power station were coated with different types of nickel-and iron-base coatings containing chromium, Fe-Cr, and Fe-Si using the powder flame spraying technique. After testing, the coated tubes were analyzed using electron microscopy. The results showed that all the coating systems had good corrosion resistance, especially those containing silicon or chromium.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.