Background: This study is aimed to evaluate the use of epithelial cells adhering the acrylic removable partial denture in establishing the sex of the individual using sex-determining region of the Y chromosome (SRY) gene. With a hypothesis that prosthetic appliance can also be used as a source of DNA in forensics for sex determination. A sample of 30 partial dentures from different denture wearers was selected for this study. Informed consent was taken from the subjects and institutional ethical clearance was obtained for this study. Samples were then washed in saline and scrapings from 0.5 × 0.5 cm 2 of the tissue contacting surface were taken using a blade of fixed thickness. DNA extraction was done from these isolated epithelial cells using Real Genomics YGB 100 (Real Biotech Corporation, Taiwan). Quantification and purity assessment of the extracted DNA was done using a Nanodrop ND-1000 spectrophotometer and clean DNA was subjected to real-time PCR amplification using SRY sex-typing marker for the detection of the presence of the SRY gene. Results: Isolation of epithelial cells and extraction of DNA from all 30 acrylic removable partial dentures were possible. Average DNA yield quantified from all samples was 32.37 ng/μl with a minimum yield of 2.17 ng/μl and a maximum yield of 117.57 ng/μl. On amplification of the target sequence, sex determination was possible from all samples with 100% accuracy. Conclusion: Acrylic removable partial denture can also be used as a source of DNA in forensics for sex identification.
The metal dual-arch trays showed better accuracy followed by the plastic dual-arch and stock dentulous trays, respectively, though statistically insignificant. The pouring sequence did not have any effect on the inter-abutment distance statistically, though pouring the non-working side of the dual-arch impression first showed better accuracy.
Aim:
To evaluate the antimicrobial potential of irreversible hydrocolloid impression material manipulated using chitosan impregnated solution at various time intervals.
Setting and Design:
Evaluative invivo study design.
Materials and Methods:
Maxillary impressions made for 20 dentulous volunteers using irreversible hydrocolloid impression material manipulated using distilled water as control and using 1% chitosan impregnated solution as test group using stock metal trays with one-week interval. Bacterial samples were collected using dry sterile cotton swab in the mid-palatal region at the time intervals of 0, 10, 20 minutes. Bacterial swabs were inoculated on nutrient agar media and incubated at 37° C for 24 hours. Bacterial colonies were counted with the aid of colony counter.
Statistical Analysis Used:
The resultant data was subjected to statistical analysis using repeated measures ANOVA and independent t test.
Results:
Adding water soluble chitosan to irreversible hydrocolloid impression material resulted in superior antimicrobial activity. With the passage of time there was a significant decrease in the microbial colony count upto 10min (p=0.016). However, the rate of decrease of microbial colony count was statistically insignificant between the samples collected at 10 and 20 min.
Conclusion:
Incorporation of water soluble chitosan to irreversible hydrocolloid impression material showed significant antimicrobial activity in 10 minutes.
Aim:
Use of silicone fit-checking material during cementation of fixed restoration has shown to leave residual silicone film after peeling off of fit checker (FC). This residual film reduced bond strength of cement to the inner surface of restoration. Silicone residue effect on tooth surface needs to be studied. The aim of this study was to evaluate the effect of residual silicone film on shear bond strength (SBS) of glass ionomer cement (GIC) to dentin surface and the efficacy of different surface treatments (STs) on dentin in the removal of silicone residue.
Materials and Methods:
Fifty freshly extracted human molars were individually mounted on acrylic blocks and occlusal surfaces were ground flat until dentine surface was exposed. Specimens were divided into five groups as follows: Group I: without application of FC (
n
= 10) as control group; Group II: without any ST after peeling off FC (
n
= 10); Group III: ST using wet pumice after peeling off FC (
n
= 10); Group IV: ST with 37% phosphoric acid after peeling off FC (
n
= 10); and Group V: ST with 10% polyacrylic acid after peeling off FC (
n
= 10). GIC was placed on the dentinal surface using polyvinyl mold and subjected to SBS test using universal testing machine. The debonded specimens were observed under stereomicroscope for the mode of failure. Selected debonded dentinal surfaces from each group were examined under scanning electron microscope. One-way analysis of variance and Tukey's test.
Results:
Group II (1.083 MPa) showed significantly lower SBS. Among the STs, Group III (2.047 MPa) was comparable to the control group whereas Group IV (1.376 MPa) and Group V (1.63 MPa) were significantly lower. There was no significant association between failures and groups at
P
= 0.257.
Conclusion:
The residue of silicone was demonstrable on dentin surface after peeling off FC and caused a significant reduction in SBS between GIC and dentin. ST with wet pumice is found to be beneficial in removing silicone residue and improving SBS, followed by phosphoric acid and polyacrylic acid.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.