AISI D6 (hardness 65 HRC) is one of the hard-to-cut steel alloys and commonly used in mould and die making industries. In general, CBN and PCBN tools are used for machining hardened steel but its higher cost makes the use for limited applications. However, the usefulness of carbide tool with selective coatings is the best substitute having comparable tool life, and in terms of cost is approximately one-tenth of CBN tool. The present study highlights a detailed analysis on machinability investigation of hardened AISI D6 alloy die steel using newly developed SPPP-AlTiSiN coated carbide tools in finish dry turning operation. In addition, a comparative assessment has been performed based on the effectiveness of cutting tool performance of nanocomposite coating of AlTiN deposited by hyperlox PVD technique and a coating of AlTiSiN deposited by scalable pulsed power plasma (SPPP) technique. The required number of machining trials under varied cutting conditions (speed, depth of cut, feed) were based on L16 orthogonal array design which investigated the crater wear, flank wear, surface roughness, chip morphology, and cutting force in hard turning. Out of the two cutting tools, newly-developed nanocomposite (SPPP-AlTiSiN) coated carbide tool promises an improved surface finish, minimum cutting force, longer tool life due to lower value of crater & flank wears, and considerable improvement in tool life (i.e., by 47.83%). At higher cutting speeds, the crater wear length and flank wear increases whereas the surface roughness, crater wear width and cutting force decreases. Chip morphology confirmed the formation of serrated type saw tooth chips.
Soda lime glass is used extensively in camera lens, micro gas turbines, light bulbs, tablewares, optics, and chemical apparatus owing to its high hardness, excellent optical properties, and good corrosion and chemical resistance. Such applications of soda lime glass demand high machining and finishing precision. On the other hand, machining of glass poses significant challenges due to its inherent brittleness. The process of removal of material from glass, if not done in ductile mode, can generate subsurface cracks and brittle fractures which have adverse effects on its functionality. This research investigates the high speed micro-end milling of soda lime glass in order to obtain ductile regime machining. It has been found by other researchers that ductile mode machining can avoid sub-surface cracks and brittle fractures. However, in ductile mode machining, the gummy chips settle permanently on the machined surface affecting adversely the surface finish. In order to avoid such chip settlement, compressed air was directed using a special air delivery nozzle to blow away the resultant gummy chips, thereby preventing them from settling on the machined surface. Response surface methodology (RSM) and a commercial NC end mill were used to design and perform the machining runs, respectively. Machining was done using: high spindle speeds from 30,000 to 50,000 rpm, feed rates from 5 to 15 mm/min, and depth of cuts from 3 to 7 μm. Three different diameter carbide tools were used: 0.5, 1, and 2 mm. A surface profilometer was used to analyze the surface roughness of the resultant machined surface. Subsequently, the data was used for finding the best combination of cutting parameters required to obtain the lowest surface roughness. The results demonstrate that high speed machining is a viable option for obtaining ductile regime machining and generating machined surfaces with very low surface roughness in the range of 0.08μm – 0.22 μm, using 0.5 mm carbide end mill cutter.
Soda lime glass is widely used in optics, chemical apparatus, camera lens, micro gas turbines, light bulbs etc. on account of its high hardness, corrosion resistance, and excellent optical properties. These require high dimensional accuracy and flawless surface finish. However, soda lime glass is inherently brittle leading to subsurface crack propagation and fracture which compromise its functionality. To avoid these defects, the machining needs to be performed under ductile mode conditions. Therefore, this research investigates the viability and requisite conditions for achieving ductile regime machining (DRM) in high speed micro-end milling of soda lime glass. Machining was performed at high cutting speeds (30,000 to 50,000 rpm), feed rate (5 to 15 mm/min), and depth of cut (3 to 7 μm). A surface profilometer was then used to measure the surface roughness and a scanning electron microscope (SEM) used to scrutinize the resultant machined surfaces. The results demonstrate that ductile streaks and rounded gummy chips (without sharp or jagged edges) are produced in all runs. In addition, there are no subsurface cracks and the minimum surface roughness attained is 0.08μm. These indicate that DRM of soda lime glass is obtainable using high-speed micro end milling in a conventional end mill with tungsten carbide inserts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.