No abstract

Ti-6Al-4V-based nanotubes were prepared on a Ti-6Al-4V surface by anodic oxidation on 10 V, 20 V, and 30 V samples. The 10 V, 20 V, and 30 V samples and a control smooth Ti-6Al-4V sample were evaluated in terms of their chemical composition, diameter distribution, and cellular response. The surfaces of the 10 V, 20 V, and 30 V samples consisted of nanotubes of a relatively wide range of diameters that increased with the voltage. Saos-2 cells had a similar initial adhesion on all nanotube samples to the control Ti-6Al-4V sample, but it was lower than on glass. On day 3, the highest concentrations of both vinculin and talin measured by enzyme-linked immunosorbent assay and intensity of immunofluorescence staining were on 30 V nanotubes. On the other hand, the highest concentrations of ALP, type I collagen, and osteopontin were found on 10 V and 20 V samples. The final cellular densities on 10 V, 20 V, and 30 V samples were higher than on glass. Therefore, the controlled anodization of Ti-6Al-4V seems to be a useful tool for preparing nanostructured materials with desirable biological properties.

The occurrence of blue-grey areas in the soft tissue represents one of the problems affecting patients whose teeth have been restored using metallic materials. It is generally accepted that it is caused by mechanical penetration of a metallic material into the soft tissue. Several facts indicate that this mechanism is not general. The aim of the study was to determine an alternative mechanism of the origin of pigmentations, based on the corrosion interaction of metallic materials used in prosthodontics with the oral environment. The study was comprised of an analysis of pigment particles, determination of exposure conditions of metallic materials in vivo and laboratory evaluation of corrosion properties of the studied materials. Particles containing silver, sulphur and/or selenium could be seen in ultra-thin sections in the lamina propria gingivae. Comparison of the corrosion laboratory results with the results of in vivo measurements indicated the intensification of corrosion under these conditions. Amalgams and silver-containing alloys used for teeth restorations may release silver under the conditions of the oral cavity. The formation of soluble silver compounds in the sulcular area or in a crevice between the crown and the cast post-and-core reconstruction facilitates their transport to the soft tissue and subsequent deposition.

No abstract

No abstract

No abstract

No abstract

The negative effect of fluoride ions on titanium has been known in dentistry for a long time. The presented work was aimed at the interaction between titanium and model saliva following a short-term exposure of a specimen to a model medical preparation rich in fluoride ions. The experimental work was carried out using titanium grade 2 in a physiological solution (pH non-adjusted, 5.8, 4.2; 5000 ppm F-) and in model saliva. Electrochemical measurement techniques were supplemented with XPS analysis. The presence of fluoride ions resulted in partial degradation of the passive layer even in a slightly acidic environment. The decrease of pH to the value of 4.2 and the presence of 5000 ppm F- caused titanium activation followed by a slow repassivation in model saliva. Formation of low soluble compound rich in fluorine explains experimental data. Short medical treatment can result in relatively long period of increased titanium corrosion.