This study aimed to evaluate the effect of different concentrations of sodium hypochlorite (NaOCl) and calcium hypochlorite [Ca(OCl)2] on the bond strength and adaptation of glass fiber posts luted with a dual-curing resin cement. Fifty decoronated premolars were sectioned 14 mm from the apex and endodontically treated. The root canal filling was partially removed. The specimens were divided into 5 groups (n=10) according to the irrigant for post space irrigation: 0.9% sodium chloride (NaCl), (control); 2.5% NaOCl; 5.25% NaOCl; 2.5% Ca(OCl)2; and 5.25% Ca(OCl)2. For each group, irrigation was performed with 5 ml of solution. Afterward, the posts were luted with a dual-curing resin cement. One slice from each third was obtained and submitted to the push-out test and failure modes analysis. An additional slice from the middle third was submitted to confocal images for analysis of adaptation failures (gaps). Two-way ANOVA, Tukey’s post-hoc, Kruskal-Wallis with Bonferroni adjusted, and chi-square tests, analyzed data. The group treated with 5.25% NaOCl showed lower bond strength values and generated more cohesive failures compared to the control (p < 0.05). Bond strength decreased from coronal to apical in the post space (p < 0.001). The groups treated with NaOCl had the highest percentages of gaps compared to the control (p < 0.05). Regardless of concentration, Ca(OCl)2 did not influence the bond strength and the occurrence of gaps (P > 0.05). Ca(OCl)2 is a good option for irrigating the post space before luting a fiber post with a dual-curing resin cement.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.