With the increased clinical interest in metal-on-metal and ceramic-on-ceramic total-hip replacements (THRs), the objective of this hip simulator study was to identify the relative wear ranking of three bearing systems, namely CoCr-polyethylene (M-PE), CoCr-CoCr (M-M) and ceramic-on-ceramic (C-C). Volumetric wear rates were used as the method of comparison. The seven THR groupings included one M-PE study, two M-M studies and four C-C studies. Special emphasis was given to defining the 'run-in' phase of accelerated wear that rigid-on-rigid bearings generally exhibit. The hypothesis was that characterization of the run-in and steady state wear phases would clarify not only the tribological performance in vitro but also help correlate these in vitro wear rates with the 'average' wear rates measured on retrieved implants. The implant systems were studied on multichannel hip simulators using the Paul gait cycle and bovine serum as the lubricant. With 28 mm CoCr heads, the PE (2.5 Mrad/N2) wear rates averaged 13 mm3/10(6) cycles duration. This was considered a low value compared with the clinical model of 74 mm3/year (for 28 mm heads). Our later studies established that this low laboratory value was a consequence of the serum parameters then in use. The mating CoCr heads (with PE cups) wore at the steady state rate of 0.028 mm3/10(6) cycles. The concurrently run Metasul M-M THRs wore at the steady state rate of 0.119 mm3/10(6) cycles with high-protein serum. In the second Metasul M-M study with low-protein serum, the THR run-in rate was 2.681 mm3/10(6) cycles and steady state was 0.977 mm3/10(6) cycles. At 10 years, these data would predict a 70-fold reduction in M-M wear debris compared with the clinical PE wear model. All M-M implants exhibited biphasic wear trends, with the transition point at 0.5 x 10(6) cycles between run-in and steady state phases, the latter averaging a 3-fold decrease in wear rate. White surface coatings on implants (coming from the serum solution) were a confounding factor but did not obscure the two orders of magnitude wear performance improvement for CoCr over PE cups. The liners in the alumina head-alumina cup combination wore at the steady state rate of 0.004 mm3/10(6) cycles over 14 x 10(6) cycles duration (high-protein serum). The zirconia head-alumina cup THR combination wore at 0.174 and 0.014 mm3/10(6) cycles for run-in and steady state rates respectively (low-protein serum). The zirconia head and cup THR combination wore slightly higher initially with 0.342 and 0.013 mm3/10(6) cycles for run-in and steady state rates respectively. Other wear studies have generally predicted catastrophic wear for such zirconia-ceramic combinations. It was noted that the zirconia wear trends were frequently masked by the effects of tenacious white surface coatings. It was possible that these coatings protected the zirconia surfaces somewhat in this simulator study. The experimental ceramic Crystaloy THR had the highest ceramic run-in wear at 0.681 mm3/10(6) cycles and typical 0.016 mm3/10(6) cycles for ...
The objective of this study is to assess whether a new biodegradable elastomer, poly(1,8-octanediol citrate) (POC), would be a suitable material to engineer elastomeric scaffolds for cartilage tissue engineering. Porous POC scaffolds were prepared via the salt-leaching method and initially assessed for their ability to rapidly recover from compressive deformation (% recovery ratio). Controls consisted of scaffolds made from other materials commonly used in cartilage tissue engineering, including 2% agarose, 4% alginate, non woven poly(glycolic acid) (PGA) meshes, and non woven poly(L-lactide-co-glycolide) (PLGA) meshes. Articular chondrocytes from bovine knee were isolated and seeded onto porous disk-shaped POC scaffolds, which were subsequently cultured in vitro for up to 28 days. POC scaffolds completely recover from compressive deformation, and the stress-strain curve is typical of an elastomer (recovery ratio>98%). Agarose gel (2%) scaffolds broke during the compression test. The recovery ratio of 4% alginate gel scaffolds, PLLA, and PGA were 72, 85, and 88%, respectively. The Young's modulus of POC-chondrocyte constructs and cell-free POC scaffolds cultured for 28 days were 12.02+/-2.26 kPa and 3.27+/-0.72 kPa, respectively. After 28 days of culture, the recovery ratio of POC-chondrocyte constructs and cell-free POC scaffolds were 93% and 99%, respectively. The glycosaminoglycan (GAG) and collagen content at day 28 was 36% and 26% of that found in bovine knee cartilage explants. Histology/immunohistochemistry evaluations confirm that chondrocytes were able to attach to the pore walls within the scaffold, maintain cell phenotype, and form a cartilaginous tissue during the 28 days of culture.
BACKGROUND:Methylnaltrexone has been shown to be effective for treating opioid-induced constipation (OIC) in chronic settings, but its effects on acute OIC have not been studied.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.