The high-volume resistivity and surface resistance of poly(ether ether ketone)/multiwalled carbon nanotubes (PEEK/MWCNT) composites restrict their use in an electronic field. To decrease the volume resistivity and surface resistance, we metalized the composites by electroless plating. The composites and metal coatings were characterized by SEM, XPS, AFM, EDX, and XRD spectroscopy. The swelling ratio of the composites, volume resistivity of two-side-coated composites, sheet resistance of plated composites, and adhesion between the coating and PEEK/MWCNT were tested. The results are as follows. A high roughness and a small swelling ratio were obtained by swelling in 18 mol/L H2SO4 for 3 min. Most of the MWCNT on the surface were still wrapped with PEEK after swelling. To expose the MWCNT, an environmentally friendly and effective etchant (MnO2-NaH2PO4-H2SO4) was used. After etching, not only were high roughness and partially exposed MWCNT obtained but also the percentage of hydrophilic groups on the surface was increased. A dense cauliflower-like Ni-P coating was produced, and the exposed MWCNT were embedded in the metal coating after electroless plating for 20 min. The coating exhibited an amorphous structure with a phosphorus content of 11.21 wt %. The volume resistivity of two-side-coated PEEK/MWCNT dropped sharply to 38 Ω·m after electroless plating for 5 min. The sheet resistance decreased with increasing the electroless-plating time, and it dropped to 0.88 Ω/square after electroless plating for 40 min. The adhesion of the coating reached the highest 5 B scale (ASTM D3359) and could even undergo the test 20 times.
Poly (propylene fumarate)/(Calcium sulfate/β-tricalcium phosphate) (PPF/(CaSO(4)/β-TCP)) is a kind of biodegradable composite designed for bone tissue engineering. The in vitro degradation behavior of this composite has been investigated in our previous study. The aim of this study was to investigate the effects of PPF molecular weight and CaSO(4)/β-TCP molar ratio on the in vivo degradation of PPF/(CaSO(4)/β-TCP) composite and the bone tissue response to PPF/(CaSO(4)/β-TCP). Total 36 PPF/(CaSO(4)/β-TCP) composite samples were implanted into 15.0 mm segmental defects in tibiae of 18 Japanese rabbits, harvested at 2, 4 and 8 weeks after the operation, and analyzed using radiographic and histological analysis to assess the in vivo degradation of the composites as well as tissue response to the implants. The in vivo degradation results show that all the samples maintained their original shape. Tissues penetrated into the pores which formed by the degradation of CaSO(4)/β-TCP spheres near the surface of the composites. The rate of in vivo degradation and pore forming increased with a decrease in PPF molecular weight and an increase in CaSO(4)/β-TCP molar ratio. No inflammatory reaction was observed after implantation, and the composites are capable of in situ pore forming. In particular, the pore forming rate can be adjusted by varying the composition of the composites. These results may indicate that PPF/(CaSO(4)/β-TCP) is a promising osteogenic scaffold for its controllable degradation rate and excellent biocompatibility.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.