HAL is a multi-disciplinary open access archive for the deposit and dissemination of scientific research documents, whether they are published or not. The documents may come from teaching and research institutions in France or abroad, or from public or private research centers. L'archive ouverte pluridisciplinaire HAL, est destinée au dépôt et à la diffusion de documents scientifiques de niveau recherche, publiés ou non, émanant des établissements d'enseignement et de recherche français ou étrangers, des laboratoires publics ou privés.
Mullite-Zirconia refractories are well known for their good resistance to corrosion and thermal shock. In this study, several mullite-zirconia composites were developed from andalusite, alumina and zircon sintered at 1600 °C for 10 hours. The samples were subjected to thermal shock carried out after heating at 1200 °C, in order to study the mechanical and thermomechanical behaviour as a function of the amount of zirconia dispersed in the mullite matrix. It appears that that the amorphous phase (SiO2), determined by X-ray diffraction, produced by the decomposition of andalusite, increases considerably with the amount of final zirconia in the composite and has a very important influence on the porosity. This amorphous phase seems also to have an important influence on the mechanical properties of the material. The characterisation of the thermomechanical behaviour (elastic properties and damage monitoring) was carried out thanks to ultrasonic techniques (US echography and Acoustic Emission). The “surprising” evolution (increase) of the Young’s modulus E of the material after being submitted to repeated thermal shocks is highlighted and explained. The acoustic emission technique carried out at high temperature and also coupled to 4-points bending tests (at room temperature) demonstrates its effectiveness for providing a better understanding of the chronology of the involved mechanisms involved at microstructural scale.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.