The study presented here investigated hydroxyapatite biomaterials implanted in soft-tissue sites in adult sheep to determine whether these materials are osteoinductive and whether the rate of osteoinduction can be increased by manipulating the composition and porosity of the implants. For the study, 16.8-mm x 5-mm discs were prepared from mixtures of hydroxyapatite and beta-tricalcium phosphate. Five mixtures of hydroxyapatite-ceramic and hydroxyapatite-cement paste forms were studied: 100 percent hydroxyapatite-ceramic (Interpore), 60 percent hydroxyapatite-ceramic, 100 percent hydroxyapatite-cement paste, 60 percent hydroxyapatite-cement paste, and 20 percent hydroxyapatite-cement paste. Biomaterials were implanted in subcutaneous and intramuscular soft-tissue pockets in 10 adult sheep. Cranial bone grafts of equal dimension were implanted as controls. One year after implantation, the volume of all biomaterials and bone grafts was determined from a computed tomographic scan, and porosity and bone formation were determined using backscatter electron microscopy. Cranial bone and the 20 percent hydroxyapatite-cement paste implants demonstrated significant volume reduction in all sites after 1 year (p < 0.001). No significant difference in volume of the remaining four biomaterials was found. There was no significant change in pore size in the ceramic implants (range, 200 to 300 micro) and in the cement-paste implants containing 60 percent hydroxyapatite or more (range, 3 to 5 nm). Pore size in the cement-paste implants containing 20 percent hydroxyapatite increased significantly with resorption of the tricalcium-phosphate component, reaching a maximum of 200 to 300 micro in the periphery, where the greatest tricalcium-phosphate resorption had occurred. Both ceramic biomaterials demonstrated lamellar bone deposition within well-formed haversian systems through the entire depth of the implants, ranging from a mean of 6.6 percent to 11.7 percent. There was minimal bone formation in the cement-paste implants containing 60 percent hydroxyapatite or more. In contrast, cement-paste implants containing 20 percent hydroxyapatite demonstrated up to 10 percent bone replacement, which was greatest in the periphery of the implants where the greatest tricalcium-phosphate resorption had occurred. This study confirms the occurrence of true osteoinduction within hydroxyapatite-derived biomaterials, when examined using backscatter techniques. In this study, the rate of osteoinduction was greatest when a porous architecture was maintained, which was best achieved in ceramic rather than cement-paste forms of hydroxyapatite. Porosity and resultant bone formation in cement-paste implants can be improved by combining hydroxyapatite with a rapidly resorbing component, such as tricalcium phosphate.
Guided bone regeneration is a promising means for reconstructing bone defects in the cranium. The present study was performed to better define those factors that affect osteogenesis in the cranium. The authors studied a single animal model, investigating the contribution of the dura, the pericranium, and the adjacent calvarial bone in the process of calvarial regeneration in both mature and immature animals. Bilateral, 100-mm2, parietal calvariectomies were performed in immature (n = 16) and mature (n = 16) rabbits. Parietal defects were randomized to one of four groups depending on the differential blockade of the dura and/or the pericranium by expanded polytetrafluoroethylene membranes. Animals were humanely killed after 12 weeks, and histometric analysis was performed to quantitate the area of the original bone defect, new bone formation, and new bone density. Bone formation was quantified separately both at the periphery and in the center of the defects. Extrasite bone formation was also quantified both on the dural and on the pericranial sides of the barriers. Bone regeneration was incomplete in all groups over the 12-week study period, indicating that complete bone healing was not observed in any group. The dura was more osteogenic than the pericranium in mature and immature animals, as there was significantly more extrasite bone formed on the dural side in the double expanded polytetrafluoroethylene barrier groups. In both the dural and the double expanded polytetrafluoroethylene barrier groups, dural bone production was significantly greater in immature compared with mature animals. The dura appeared to be the source of central new bone, because dural blockade in the dural and double expanded polytetrafluoroethylene groups resulted in a significant decrease in central bone density in both mature and immature animals. Paradoxically, isolation of the pericranium in mature animals resulted in a significant reduction in total new bone area, whereas pericranial contact appeared to enhance peripheral new bone formation, with the control group having the greatest total new bone area. The present study establishes a model to quantitatively study the process of bone regeneration in calvarial defects and highlights differences in the contribution of the dura and pericranium to calvarial bone regeneration between infant and adult animals. On the basis of these findings, the authors propose that subsequent studies in which permeability of the expanded polytetrafluoroethylene membranes is altered to permit migration of osteoinductive proteins into the defect while blocking prolapse of adjacent soft tissues may help to make guided bone regeneration a realistic alternative for the repair of cranial defects.
Transforming growth factor-betas (TGF-beta) have been demontstrated to be upregulated during osteoblast function in vitro and during cranial suture fusion in vivo. The authors hypothesized that spontaneous reossification of calvarial defects was also associated with upregulation of TGF-beta. The present study was designed to (1) evaluate the concept of a critical-size defect within the calvaria in an adult guinea pig model and (2) investigate the association between the ossification of calvarial defects and TGF-beta upregulation. Paired circular parietal defects with diameters of 3 and 5 mm and single parietal defects with diameters of 8 or 12 mm were made in 45 six-month-old skeletally mature guinea pigs. Three animals per defect size were killed after survival periods of 3 days, 1 week, 4 weeks, 8 weeks, or 12 weeks. New bone ingrowth was evaluated by assessing for linear closure by a traditional linear method and by a modified cross-sectional area method using an image analysis system in which the thickness of new bone was taken into account. Immunohistochemistry was performed using rabbit polyclonal antibodies to localize TGF-beta1, -beta2, and -beta3. All specimens were photographed, and the intensity of immunostaining was graded based on subjective photographic assessment by three independent reviewers. No defect demonstrated any measurable bone replacement after a survival period of 3 days. All 3- and 5-mm defects were completely reossified after 12 weeks based on the linear analysis of new bone, indicating these defects to be less than critical size. However, new bone formation in the 5-mm defects never exceeded a mean of 40 percent by cross-sectional area of new bone. Percent of new bone formation by cross-sectional area was significantly higher within 3-mm defects than in all larger defects 4 weeks after the craniotomy, reaching a mean of 89 percent new bone by 12 weeks. Persistent gaps were noted on linear analysis of the 8- and 12-mm wounds by 12 weeks, and mean percent new bone by cross-sectional area remained below 30 percent. Immunolocalization demonstrated osteogenic fronts at the advancing bone edge and the endocranial side, in which the osteoblasts stained strongly for all isoforms of TGF-beta. The intensity of osteoblast expression waned considerably after the majority of the defect had reossified. These data indicate that histometric analysis based on cross-sectional area more accurately reflects the osteogenic potential of a cranial defect than does linear inspection of defect closure. Although the interpretation of immunolocalization studies is highly subjective, independent assessment by three reviewers indicates that isoforms of TGF-beta were upregulated during a limited "window" of time corresponding to the period of active calvarial reossification, and expression of TGF-beta corresponded to osteoblast activity within osteogenic fronts.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.