This paper explored the effect of adding organic fibers from either bamboo or sugarcane on the mechanical properties of concrete. Cylindrical and prismatic specimens were made containing 2% and 5% v/w (volume to weight) of vegetable fibers to concrete. Following 28 days of curing period, the samples were evaluated for compressive strength, tensile strength using diametric compression, tensile strength during bending and static modulus. It was discovered that all concretes produced met the minimum strength of 20 MPa recommended by NBR 6118 for structural purposes, and it was observed an increase of the compressive strength on the specimens with addition of organic fibers. Moreover, an increase in the compressive strength was observed in the specimens with fiber addition, although no significant variation of water absorption was noticed when compared with the standard concrete. In conclusion, the concrete containing 2% v/w of bamboo fibers showed better mechanical strength and static modulus of elasticity when compared to both concrete with sugar cane fibers addition and the concrete without any additional fibers.
ResumoEste trabalho propõe avaliar a atuação do polietileno tereftalato (PET) como um agregado substituto na fabricação de concreto para pavers, pavimento intertravado com peças de concreto, a fim de minimizar os efeitos colaterais da construção civil. PET triturado substituiu o agregado natural, pó de pedra, nas porcentagens de 10%, 15% e 20% em massa. Os testes mecânicos de resistência à compressão realizado aos 28 dias mostraram que os corpos de prova moldados a partir dos traços substituídos apresentaram significativa melhora da resistência à compressão, que a substituição parcial de 10% em massa de PET atende ao recomendado pela NBR 9781 (2013) para concreto para pavimentação e que todos os concretos produzidos atendem a resistência mínima a compressão de 20 MPa, recomendado pela NBR 6118 (2003) para concreto estrutural. Palavras-chave:PET; Pavers; Resistência à compressão; Construção civil. STUDY OF PARTIAL REPLACEMENT OF STONE POWDER FOR PET TO PAVERS MANUFACTURE AbstractThis work proposes the performance evaluation of polyethylene terephthalate (PET) as an aggregate replacement in the concrete manufacturing for interlocking concrete pavements, in order to minimize the side effects of the construction industry. Crushed PET replaced the natural aggregate, stone dust, in percentages of 10%, 15% and 20% by mass. The compressive strength test performed after 28 days showed that the specimens molded from the replaced mix showed significant improvement in compared to specimens molded by the reference mix PET in percentages of 10% by mass meets the minimum strength of 35 MPa recommended by NBR 9781 (2013) for pavers and all concretes produced meets the minimum strength of 20 MPa recommended by NBR 6118 (2003) for structural concrete.
ResumoO fenômeno de crepitação de minérios de ferro ocorre durante o processo de redução do minério de ferro em altos-fornos e é uma fonte geradora de finos devido à sua degradação granulométrica. Os finos em excesso prejudicam a permeabilidade da carga e diminui o rendimento da produção de ferro-gusa. No presente trabalho, foi realizado um estudo da crepitação de minérios de ferro através do emprego de um sistema de pré-tratamento térmico do minério de ferro a partir do gás de topo no processo de produção de ferro-gusa de um mini alto-forno a carvão vegetal em uma empresa situada de Minas Gerais. Foram utilizados dois períodos de sete dias cada, sendo que no primeiro período o sistema de pré-tratamento do minério estava desativado e no segundo o sistema foi ativado. Os resultados demonstraram uma melhora nas propriedades do minério de ferro quando se utiliza o pré-tratamento com o gás de topo, pois resultou num aumento de produção por amenizar o fenômeno de crepitação. Palavras-chave: Gases de exaustão; Alto-forno; Crepitação do minério de ferro; Pré-aquecimento da matéria-prima. AbstractThe phenomenon of particle size degradation of minerals due to decreptation is presented as source of fines. In the present work, a study of iron ores decrepitation by employing a system of thermal pretreatment of iron ore was carried out reusing exhaust gases from a mini charcoal blast furnace located in the state of Minas Gerais. The experiments were carried out in two periods of seven days each one, where in the first period the pretreatment system was deactivated and in the second period was activated. The results showed an improvement in the burden permeability by the reduction of the granules decreptation when it was used the thermal pretreatment, reflecting in a increasing of production.
ResumoO presente trabalho tem como objetivo estudar a influência da adição do rejeito de pó de balão nas propriedades mecânicas do concreto destinado à fabricação de pavers, visto que a indústria da construção civil é a maior responsável pela geração de resíduos, sendo responsável pelo consumo de aproximadamente 40% dos recursos naturais extraídos. Sendo assim, o rejeito foi analisado granulometricamente por peneiramento e foram feitos dois traços, um denominado traço referência e o outro denominado traço substituído, sendo este último com adição de 4% em massa do pó de balão. A partir dos traços calculados foram moldados corpos de prova e avaliados a resistência à compressão destes. Os corpos de prova moldados a partir do traço substituído exibiram maior resistência à compressão tanto na idade de 7 dias quanto na idade de 28 dias, quando comparados aos corpos moldados a partir do traço referência. Esse incremento na resistência mecânica é justificado pela distribuição granulométrica do pó de balão, que por ser constituído em sua maior parte por finos inferiores a 0,15mm atua preenchendo vazios, reduzindo zonas de transição interfacial e formando uma microestrutura mais refinada. Palavras-chave: Pó de balão; Pavers; Resistência à compressão; Construção civil. STUDY OF THE PARTIAL REPLACEMENT OF STONE DUST BY BALLON POWDER IN PRECAST CONCRETE BLOCKS AbstractThe presente work aims to study the influence of the addition of balloon powder waste on the mechanical properties of concrete used to manufacture pavers, since the construction industry is the main responsible for the generation of waste, being responsible for the consumption of approximately 40% of all mined natural resources.Therefore, the waste was granulometrically analysed by sieving and two diferente concrete dosages were made. The first one was called reference dosage and the second one was named substituted dosage, being the latter with addition of 4% in mass of balloon powder. Using the concrete dosages calculated, concrete samples were made and their compressive strenght was evaluated. The concrete samples made from the substituted dosage showed higher compressive strenght in the age of 7 days as well as in the age of 28 days, when compared to the reference dosage. This higher compressive strenght is justified by the particle size distribution of the balloon powder, which consist mostly of thin particles below 0.15mm, that act filling empty spaces, reducing interfacial transition zones and forming a more refined microstructure.
O ensino de ciências é uma das áreas mais importantes para a formação de pessoas preparadas para lidar com os avanços da tecnologia, da pós-modernidade e da cidadania, e, para tanto, torna-se interessante atrair jovens para esse saber. No Brasil existe um certo “desencanto” dos estudantes em relação às licenciaturas em ciências e matemática, e tornou-se um desafio para os autores buscarem formas de atrai-los para essas licenciaturas. Considerou-se, como forma de se trabalhar esse desencantamento, motivar os estudantes ao abordar temas como a cidadania e a transdisciplinaridade das ciências, e de que há axiomas comuns às ciências como um todo ou a um conjunto de disciplinas. Este estudo visa, assim, apresentar um projeto cidadão e transdisciplinar concebido para o incentivo aos jovens às carreiras de ensino de ciências. Realizou-se, portanto, um relato de caso de um projeto transdisciplinar realizado no Município de Itabira - MG voltado para a Semana Nacional de Ciência e Tecnologia. Os resultados dos trabalhos transdisciplinares executados mostraram que houve um aumento na motivação dos estudantes para carreiras docentes na área da ciência e tecnologia.
ResumoEste trabalho objetiva o estudo da influência da adição de fibras vegetais de bambu e cana-deaçúcar nas propriedades mecânicas do concreto. Para este trabalho foram confeccionados corpos-de-prova cilíndricos e prismáticos nos quais foram adicionados 2% e 5% em volume das fibras à massa do concreto. Após a cura, conforme NBR 5738 (2003) [1], os mesmos foram testados via ensaios de resistência à compressão conforme NBR 5739 (2007) [2], resistência à tração por compressão diametral, conforme NBR 7222 (2011) [3], resistência à tração na flexão conforme NBR 12142 (2010) [4] e módulo de elasticidade estático, conforme NBR 8522 (2008) [5]. Verificou-se após os testes que todos os concretos produzidos atenderam a resistência mínima a compressão de 20 MPa, recomendado pela NBR 6118 (2003) [6] para fins estruturais. Foi observado um aumento da resistência à compressão em relação à mistura padrão. O concreto com adição de fibras de bambu apresentou melhor resistência mecânica em relação ao concreto com adição das fibras de cana-de-açúcar e ao concreto sem adição. Abstract This work aimed to study the influence of the addition of vegetable fibers from bamboo and sugar cane on the mechanical properties of concrete. Implementing the same body-of-proof cylindrical and prismatic, which were added 2% to 5% per volume of fibers to the mass of concrete were made. After healing according to NBR 5738 (2003) [1], they were tested by testing of compressive resistance, according to NBR 5739 (2007) [2], tensile strength by diametric compression according to NBR 7222(2011) [3], tensile strength in bending according to NBR 12142 (2010) [4] and static modulus, according to NBR 8522(2008) [5]. It was found after testing all concretes produced met the minimum strength of 20 MPa recommended by NBR 6118 (2003) [6] for structural purposes. An increased compression resistance compared to the standard mixture was observed. The concrete with added bamboo fibers showed better mechanical strength compared to concrete with the addition of sugar cane sugar and plain concrete fibers.
This research aims to estimate the design costs of implementing the bioconcrete samples suitable for structural purposes. The bioconcrete samples were produced by adding specific bacteria, Sporosarcina pasteurii. The specimens were submitted to tests of resistance to axial compression according to ABNT NBR 5739 under water-curing periods of 7, 14, and 28 days. To the implementation of this research, it was necessary execution of some stages: bibliographic research, and the providing of better visualization of the theme. The initial acquisition of bacteria, then the cultivation of bacteria to incorporate in the concrete. The third stage was laboratory tests to analyze the new concrete and make reports and data tabulation. The early costs results are encouraging further study.
The performance of the mineral productive sector is performed through indices that measure the efficiency of a process. tools such as control charts monitor the variability and stability of a process, evaluating whether it conforms to the optimum condition or not, through performance indicators. In this paper, we used the combination of importing a mining company's dispatch software database (Smartmine®) along with Power BI, which is a free service analysis software provided by Microsoft to produce performance indicators to support the simultaneous reports that support the managers in the choice of the best performance condition, either in the decision making by the mining management team, or in the maintenance, equipment exchange and reformulation of maintenance strategies.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.