Dual-phase (DP) steels are produced from a specific heat treatment procedure and have recently emerged as a potential class of engineering materials for a number of structural and automobile applications. Such steels have high strength-to-weight ratio and reasonable formability. The present study aims to investigate the effects of four different and conventional heat treatments (i.e., hot rolling, normalizing, annealing, and intercritical annealing) on the resulting microstructural patterns and on the electrochemical corrosion behavior. Electrochemical impedance spectroscopy (EIS) and Tafel plots were carried out on heat treated steel samples in a 0.5 M NaCl solution at 25 8C with neutral pH. An equivalent circuit analysis was also used to provide quantitative support for the discussions. The normalizing and the annealing heat treatments have provided the highest and the lowest corrosion resistances, respectively. The intercritical annealing and as-received (hot rolled) low carbon steel samples have shown similar corrosion behavior. Although a deleterious effect on the corrosion resistance has been verified for DP steel due to the residual stress from the martensite formation, it combines good mechanical properties with intermediate electrochemical corrosion resistance.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.