This study investigated the effect of hemp fiber pretreatments (water and sodium hydroxide) combined with silane treatment, first on the fiber properties (microscale) and then on polylactide (PLA) composite properties (macroscale). At the microscale, Fourier transform infrared, thermogravimetric analysis, and scanning electron microscopy investigations highlighted structural alterations in the fibers, with the removal of targeted components and rearrangement in the cell wall. These structural changes influenced unitary fiber properties. At the macroscale, both pretreatments increased the composites’ tensile properties, despite their negative impact on fiber performance. Additionally, silane treatment improved composite performance thanks to higher performance of the fibers themselves and improved fiber compatibility with the PLA matrix brought on by the silane couplings. PLA composites reinforced by 30 wt.% alkali and silane treated hemp fibers exhibited the highest tensile strength (62 MPa), flexural strength (113 MPa), and Young’s modulus (7.6 GPa). Overall, the paper demonstrates the applicability of locally grown, frost-retted hemp fibers for the development of bio-based composites with low density (1.13 to 1.23 g cm−3).
The effects of surface pretreatment (water and alkali) and modification with silane on moisture sorption, water resistance, and reaction to fire of hemp fiber reinforced polylactic acid (PLA) composites at two fiber loading contents (30 and 50 wt.%) are investigated in this work. Moisture adsorption was evaluated at 30, 50, 75 and 95% relative humidity, and water resistance was determined after a 28-day immersion period. The cone calorimetry technique was used to investigate response to fire. The fiber surface treatment resulted in the removal of cell wall components, which increased fiber individualization and homogeneity as shown in scanning microscopic pictures of the composite cross-section. Although the improved fiber/matrix bonding increased the composite’s water resistance, the different fiber treatments generated equal moisture adsorption results for the 30 wt.% reinforced composites. Overall, increasing the fiber amount from 30 to 50 wt.% increased the composite sensitivity to moisture/water, mainly due to the availability of more hydroxyl groups and to the development of a higher pore volume, but fire protection improved due to a reduction in the rate of thermal degradation induced by the reduced PLA content. The new Oswin’s model predicted the composite adsorption isotherm well. The 30 wt.% alkali and silane treated hemp fiber composite had the lowest overall adsorption (9%) while the 50 wt.% variant produced the highest ignition temperature (181 ± 18 °C).
The present study investigated the effect of biochar (BC) addition on mechanical, thermal, and water resistance properties of PLA and hemp-PLA-based composites. BC was combined with variable concentration to PLA (5 wt%, 10 wt%, and 20 wt%) and hemp (30 wt%)-PLA (5 wt% and 10 wt%); then, composites were blended and injection molded. Samples were characterized by color measurements, tensile tests, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and water contact angle analysis. Experimental results showed that adding 5 wt% of BC enhanced the composite’s tensile modulus of elasticity and strength. Hence, the use of optimized loading of BC improved the mechanical strength of the composites. However, after BC addition, thermal stability slightly decreased compared with that of neat PLA due to the catalytic effect of BC particles. Moreover, the water-repelling ability decreased as BC content increased due to the specific hydrophilic characteristics of the BC used and its great porosity.
Frost-retted hemp fibers were investigated to assess their suitability for composite applications. Chemical analysis of frost-retted hemp fibers highlighted a high amount of solubles (pectins) at the fibers surface and a low lignin content in the fibers that was attributed to an unfavorable synthesis of lignin in the cell wall due to the particularly cold temperature during hemp growth in the Nordic countries. The fibers tensile properties were considered at two different scales and the performances of hemp/PLA composites were assessed. Recommendations were provided for the use of frost-retted hemp fibers in the reinforcement of thermoplastic composites.
The presented research aimed at finding new ways to value hemp by-products (stalks) from the cannabidiol industry through thermochemical conversion. Chemical and elemental composition of hemp biomass was investigated by successive chemical extractions and Scanning Electron Microscopy along with Energy-dispersive X-ray Spectroscopy. Proximate and elemental analyses completed the chemical characterization of the hemp biomass and its biochar. Thermogravimetric analysis of the hemp biomass allowed to understand its kinetic of decomposition during thermal conversion. The carbon structure and porosity of the biochar were assessed by Raman spectroscopy and CO2 gas adsorption. Properties of interest were the energy production measured through calorific values, and the electrical conductivity. Two ways of valorisation of the hemp biomass were clearly identified, depending mainly on the chosen pyrolysis temperature. Hemp biochar carbonized at 400–600°C were classified as lignocellulosic materials with a good potential for solid biofuel applications. Specifically, the resulting carbonized biochar presented low moisture content (below 2.50%) favourable for high fuel quality, low volatile matter (27.1–10.4%) likely to show lower particle matter emissions, limited ash content (6.8–9.8%) resulting in low risk of fouling issues during the combustion, high carbon content (73.8–86.8%) suggesting strong energy density, associated with high higher heating values (28.45–30.95 MJ kg−1). Hemp biochar carbonized at 800–1000 °C displayed interesting electrical conductivity, opening opportunities for its use in electrical purposes. The electrical conductivity was related to the evolution of the biochar microstructure (development of graphite-like structure and changes in microporosity) in regard with the thermochemical conversion process parameters.
Graphical abstract
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.