The surface chemistry of D 2 O dosed Zircaloy-4 (Zry-4) surface followed by Ar-ion bombardment and annealing was studied by means of X-ray photoelectron spectroscopy (XPS) and Ultraviolet photoelectron spectroscopy (UPS). In the XPS study, Ar-ion bombardment caused decrease of the oxygen on the surface region of Zry-4 and therefore led to change the oxidation states of the zirconium from oxide to metallic form. In addition, oxidation states of zirconium were changed to lower oxidation states of zirconium due to depopulation of oxygen on the surface region by annealing. Up to about 787 K, the bulk oxygen diffused out to the subsurface region and after this temperature, the oxygen on the surface of Zry-4 was depopulated. UPS study showed that the valence band spectrum of the D 2 O exposed Zry-4 exhibited a dominant peak at around 13 eV and no clear Fermi edge was detected. After stepwise Ar + sputtering processes, the decrease of the oxygen on the surface of Zry-4 led to suppress the dominant peak around 13 eV, the peak around 9 eV and develop a new peak of the metallic Zr 4d state (20.5-21.0 eV) at the Fermi level.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.