Microstructure and shear strength of Sn-Zn lead-free solders and Au/Ni/Cu UBM joint under thermal aging conditions were investigated. The samples were aged isothermally at 373 K and 423 K for 300, 600, and 900 hours. The IMCs at the interface between solder and UBM were examined by FESEM and TEM. The results showed the shear strength was decreased with aging time and temperature. The solder ball with highly activated flux had about 8.2% increased shear strength than that of BGA/CSP flux. Poor wetting and many voids were observed in the fractured solder joint with of the latter flux. The decreased shear strength was caused by IMC growth and Zn grain coarsening. In the solder layer, Zn reacted with Au and then was transformed to the -AuZn compound. At the joint interface, although AuZn grew first, -Ni 5 Zn 21 compounds were formed with aging time.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.