In this study, basalt fiber-reinforced polymer (BFRP) composites with epoxy matrix, 20 layers, and volume fraction of fibers Vf = 53.66%, were prepared by a hand lay-up compression molding combined method. The fabric of the basalt fibers is in twill 2/2 weave. Through dynamic mechanical analysis (DMA), their viscoelastic behavior at elevated temperatures and in various frequencies was explored, whereas thermomechanical analysis (TMA) took part in terms of creep recovery and stress-relaxation tests. Moreover, the glass transition temperature (Tg) of the BFRP composites was determined through the peak of the tanδ curves while the decomposition of the BFRP composites and basalt fibers, in air or nitrogen atmosphere, was explored through thermogravimetric analysis (TGA). The mechanical behavior of the BFRP composites was investigated by tensile and three-point bending experiments. The results showed that as the frequency is raised, the BFRP composites can achieve slightly higher Tg while, under the same circumstances, the storage modulus curve obtains a less steep decrease in the middle transition region. Moreover, the hand lay-up compression molding hybrid technique can be characterized as efficient for the preparation of polymer matrix composites with a relatively high Vf of over 50%. Remarkably, through the TGA experiments, the excellent thermal resistance of the basalt fibers, in the temperature range 30–900 °C, was revealed.
This article deals with the lifetime of laminated materials produced by different production technologies (hand lamination technology, vacuum bagging technology and prepreg technology with curing in the oven) during cyclic repeated bending stress. Like tested materials composite systems were chosen composite systems with epoxy matrix and carbon reinforcement (Kordcarbon CC200T, epoxy resin with trade name L285) and second composite epoxy system with glass reinforcement (Quadra-axial glass fabric, named Saertex Q-E-820, epoxy resin Biresin CR 82 and third prepreg systems (unidirectional prepreg, trade name Deltapreg VV430U-DT860W-39% and prepreg system with glass fabric VV320P_DT806R-37%). Fatigue tests were performed by cyclic bending loads during a three-point arrangement on a universal servo-hydraulic testing machine INSTRON 8871. Experimentally the number of cycles fracture of the material was determined at 90 % and 80 % of the maximum breaking load.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.