Heteroepitaxial growth is critical for large-scale synthesis of diamond (111) substrates. In this study, the local initial epitaxial growth of diamond (111) on Ru/c-sapphire was investigated. As the economic viability of ruthenium (Ru) is more than that of iridium (Ir), a 150-nm Ru (0001) thin film was sputter-deposited on an Al2O3 (0001) substrate using a RF/DC magnetron sputtering system. X-ray diffraction analyses of the Ru film revealed the (0001) phase orientation with high crystalline quality. Both bias-enhanced nucleation and initial heteroepitaxial growth of diamond were realized via antenna-edge-type microwave plasma chemical vapor deposition. After 30 min of heteroepitaxial growth, the crystallite (diameter ∼500 nm) with a smooth surface was observed through scanning electron microscopy. Electron backscattering diffraction (EBSD) orientation mapping indicated the presence of the highly oriented diamond (111) crystallite. The epitaxial orientations between diamond (111) and Ru were determined as [111]diamond//[0001]Ru and [112¯]diamond//[101¯0]Ru. The EBSD pole-figure pattern represented the formation of a double positioning defect. This study demonstrated the feasibility of heteroepitaxial growth of diamond (111) on Ru, which provides a more economically viable approach to fabricating large-size diamond substrates.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.