Samples of spent bleaching clay were deoiled by hexane, methanol, hexane-methanol, and supercritical CO 2 extractions. The deoiled clays were regenerated by acid and heat treatments. Nitrogen adsorption isotherms for these samples are type IV with hysteresis loops corresponding to type H3, indicating slit-shaped pores. Used deoiled and dried samples have smaller surface areas and pore volumes than unused clay. The surface areas and pore volumes increased after heat treatment. Acidified heat-treated deoiled samples have smaller surface areas and greater pore volumes than unused clay, except for the methanol-deoiled sample. Thus, heat and acid treatments removed substances adsorbed in the pores that were not removed by solvents or CO 2 extraction. This was confirmed from the ratios of the cumulative surface area/BET surface area, as well as analysis of the pore size distributions, which indicated an increase in mesopores with radii of between 25 and 100 Å. The t-plots showed that smaller pores with sizes between 7 and 25 Å, present originally in the unused clays, were closed by heat treatment. These pores were absent in the deoiled and the heattreated samples except for the heat-treated sample that was deoiled by hexane followed by methanol. Smaller pores, accompanied by an increase in surface area, were also observed for all deoiled samples after acid and heat treatments. JAOCS 74, 963-970 (1997).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.