There is growing interest in the development of innovative cementitious materials that possess superior properties. A relatively new cementitious material, reactive powder concrete, is recognised as a revolutionary material that provides a combination of ultra-high strength and excellent durability. However, production of reactive powder concrete is not yet available with the limited research in this area in Hong Kong. This paper investigates mechanical and fresh concrete properties of reactive powder concrete, aiming to achieve the optimal conditions for producing reactive powder concrete using local materials by investigating the material composition, curing and heating regimes and the microstructure of reactive powder concrete. Based on the experimental results, it is found that reactive powder concrete with a water-to-binder ratio of 0 . 2, superplasticiser dosage of 2 . 5%, 150-600 ìm quartz sand cured at 278C in water condition provides the best results in terms of mechanical and composite properties as well as for practical and economical reasons, although heat treatment of the reactive powder concrete can result in a significant increase in compressive strength.
Reactive powder concrete is a relatively new cementitious material. Its main features include a high percentage ingredient of Portland cement, very low water-to-binder (cement + silica fume) ratio, a high dosage of superplasticiser and the presence of very fine crushed quartz and silica fume. Coarse aggregate in normal aggregate concrete is completely replaced by fine quartz sand with particle sizes ranging from 150 to 600 ìm. Reactive powder concrete is characterised by ultra-high performance in mechanical properties, particularly in compressive strength; and this could be of tremendous interest to construction practitioners. However, production of reactive powder concrete is not yet available in Hong Kong and limited research is available in this area. This study is an attempt to produce reactive powder concrete using local materials under laboratory conditions. Concrete designed from reactive powder concrete and high-performance concrete is experimentally conducted and compared. The results show that the compressive strength, splitting tensile strength and static modulus of elasticity are found to be significantly higher than that of high-performance concrete using the same water-to-binder ratio. It is noted that the rate of strength development of the reactive powder concrete samples is greater than that of high-performance concrete. The difference in strength at a later age is even bigger. Compressive strength of about 200 MPa could even be achieved in 3 days for the reactive powder concrete samples when the samples were heat-treated at a temperature of about 2508C for 16 h, which can be explained by the formation of xonotlite under scanning electron microscopy investigation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.