A freestanding GaN substrate over 2 inches in size was successfully prepared for the first time by hydride vapor phase epitaxy (HVPE) using GaAs as a starting substrate. In the experiment, a GaAs (111)A substrate with a SiO 2 mask pattern on its surface was used. A thick GaN layer was grown on the GaAs substrate at 1030 • C through the openings in the SiO 2 mask. By dissolving the GaAs substrate in aqua regia, a freestanding GaN substrate about 500 µm thick was obtained. The fullwidth at half maximum (FWHM) in the ω-mode X-ray diffraction (XRD) profile of GaN (0002) plane was 106 arcsec. The dislocation density of the GaN substrate obtained was determined to be as low as 2 × 10 5 cm −2 by plan-view transmission electron microscopy (TEM). Hall measurements revealed the n-type conductivity of the GaN substrate with typical carrier concentration and carrier mobility of 5 × 10 18 cm −3 and 170 cm 2 ·V −1 ·s −1 , respectively.