This is a review article on the current status and future prospects of the research and development on gallium oxide (Ga 2 O 3 ) power devices. Ga 2 O 3 possesses excellent material properties, in particular for power device applications. It is also attractive from an industrial viewpoint since large-size, high-quality wafers can be manufactured from a single-crystal bulk synthesized by melt-growth methods. These two features have drawn much attention to Ga 2 O 3 as a new wide bandgap semiconductor following SiC and GaN. In this review, we describe the recent progress in the research and development on fundamental technologies of Ga 2 O 3 devices, covering single-crystal bulk and wafer production, homoepitaxial thin film growth by molecular beam epitaxy and halide vapor phase epitaxy, as well as device processing and characterization of metal-semiconductor field-effect transistors, metal-oxide-semiconductor field-effect transistors and Schottky barrier diodes.

Ga2O3 field-plated Schottky barrier diodes (FP-SBDs) were fabricated on a Si-doped n−-Ga2O3 drift layer grown by halide vapor phase epitaxy on a Sn-doped n+-Ga2O3 (001) substrate. The specific on-resistance of the Ga2O3 FP-SBD was estimated to be 5.1 mΩ·cm2. Successful field-plate engineering resulted in a high breakdown voltage of 1076 V. A larger-than-expected effective barrier height of 1.46 eV, which was extracted from the temperature-dependent current–voltage characteristics, could be caused by the effect of fluorine atoms delivered in a hydrofluoric acid solution process.

We derive a dielectric function tensor model approach to render the optical response of monoclinic and triclinic symmetry materials with multiple uncoupled infrared and far-infrared active modes. We apply our model approach to monoclinic β-Ga 2 O 3 single-crystal samples. Surfaces cut under different angles from a bulk crystal, (010) and (201), are investigated by generalized spectroscopic ellipsometry within infrared and far-infrared spectral regions. We determine the frequency dependence of 4 independent β-Ga 2 O 3 Cartesian dielectric function tensor elements by matching large sets of experimental data using a point-by-point data inversion approach. From matching our monoclinic model to the obtained 4 dielectric function tensor components, we determine all infrared and far-infrared active transverse optic phonon modes with A u and B u symmetry, and their eigenvectors within the monoclinic lattice. We find excellent agreement between our model results and results of density functional theory calculations. We derive and discuss the frequencies of longitudinal optical phonons in β-Ga 2 O 3 . We derive and report density and anisotropic mobility parameters of the free charge carriers within the tin-doped crystals. We discuss the occurrence of longitudinal phonon plasmon coupled modes in β-Ga 2 O 3 and provide their frequencies and eigenvectors. We also discuss and present monoclinic dielectric constants for static electric fields and frequencies above the reststrahlen range, and we provide a generalization of the Lyddane-Sachs-Teller relation for monoclinic lattices with infrared and far-infrared active modes. We find that the generalized Lyddane-Sachs-Teller relation is fulfilled excellently for β-Ga 2 O 3 .

We investigated the temperature-dependent electrical properties of Pt/Ga2O3 Schottky barrier diodes (SBDs) fabricated on n–-Ga2O3 drift layers grown on single-crystal n+-Ga2O3 (001) substrates by halide vapor phase epitaxy. In an operating temperature range from 21 °C to 200 °C, the Pt/Ga2O3 (001) Schottky contact exhibited a zero-bias barrier height of 1.09–1.15 eV with a constant near-unity ideality factor. The current–voltage characteristics of the SBDs were well-modeled by thermionic emission in the forward regime and thermionic field emission in the reverse regime over the entire temperature range.

Thick high-purity β-Ga2O3 layers of high crystalline quality were grown homoepitaxially by halide vapor phase epitaxy (HVPE) using gaseous GaCl and O2 on (001) β-Ga2O3 substrates prepared by edge-defined film-fed growth. The surface morphology and structural quality of the grown layer improved with increasing growth temperature. X-ray diffraction ω-rocking curves for the (002) and (400) reflections for the layer grown at 1000 °C had small full widths at half maximum. Secondary ion mass spectrometry and electrical characteristics revealed that the growth of high-purity β-Ga2O3 layers with low effective donor concentration (Nd − Na < 1013 cm−3) is possible by HVPE.