A diarylethene fused trimer, 1-(5-(2-(3,5-dimethyl-2-thienyl)hexafluorocyclopententen-1-yl)-2,4-dimethyl-3-thienyl)-2-(5-(2-(2,4-dimethyl-5-phenyl-3-thienyl)hexafluorocyclopentene-1-yl)-2,4-dimethyl-3-thienyl)hexafluorocyclopentene, was synthesized. The diarylethene derivative showed full-color photochromic performance by choosing appropriate wavelength of light.
Self-assembled microstructures of an amphiphilic diarylethene featuring an alkyl chain and triethylene glycol groups showed a photoinduced reversible morphological change in water. Reversible photoisomerization of the core diarylethene gave rise to a reversible morphological transformation between colorless microspheres and colored fibers. When colorless microspheres were irradiated with UV light, colored fibers were formed, and when the colored fibers were irradiated with visible light, the spheres were restored to their original positions where the spheres originally existed. This system showed reversible morphological change through not only photoirradiation but also temperature change. These behaviors can be interpreted as a phase transition between the sphere and fiber states. The dynamic process of the phase transition was monitored by polarized optical microscopy (POM), transmission electron microscopy (TEM), and X-ray diffraction (XRD). It was revealed that the formation of fibers upon UV irradiation occurred radially at the surface of the sphere and the formation of the spheres upon visible-light irradiation occurred at the middle of the fiber. The unique photoinduced mechanical motion provides useful information for the design of sophisticated photoactuators.
Giving color to data recording: Upon irradiation with selected wavelengths of light the hexane solution of a fused dithienylethene derivative changes from colorless to yellow, green, black, or blue depending on the wavelength, and irradiation time (see picture). This could be a landmark in the development of new data recording materials.
We achieved drain-current switching of diarylethene-channel field-effect transistors with light- and electric-field effects. The drain current was reversibly changed by alternating ultraviolet and visible light irradiation. Stress is placed on the fact that the on/off ratio realized by light irradiation was 1 × 10(2) (1 × 10(4)%) and this value is much larger than those in other photochromism-based transistors. These results indicate that the drain current was effectively controlled by light irradiation. Furthermore, the on and off states modulated by light were maintained without light irradiation even after 1 week, exhibiting that our transistor works as an optical memory. We clarified that the light-driven modulation can be attributed to the transformation in the π-conjugation system accompanied by photoisomerization. These findings have the potential to attain high-performance optoelectrical organic devices including optical sensors, optical memory, and photoswitching transistors.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.