Hydrogenated ZnO thin films have been successfully deposited on glass substrates via a nitrogen mediated crystallization (NMC) method utilizing RF sputtering. Here we aim to study the crystallinity and electrical properties of hydrogenated NMC-ZnO films in correlation with substrate temperature and H2 flow rate. XRD measurements reveal that all the deposited films exhibit strongly preferred (001) orientation. The integral breadth of the (002) peak from the hydrogenated NMC-ZnO films is smaller than that of the conventional hydrogenated ZnO films fabricated without nitrogen. Furthermore, the crystallinity and surface morphology of the hydrogenated NMC-ZnO films are improved by increasing substrate temperature to 400 °C, where the smallest integral breadth of (002) 2θ–ω scans of 0.83° has been obtained. By utilizing the hydrogenated NMC-ZnO films as buffer layers, the crystallinity of ZnO:Al (AZO) films is also improved. The resistivity of AZO films on NMC-ZnO buffer layers decreases with increasing H2 flow rate during the sputter deposition of buffer layers from 0 to 5 sccm. At a H2 flow rate of 5 sccm, 20-nm-thick AZO films with low resistivity of 1.5×10-3 Ω cm have been obtained.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.