Additive manufacturing, aka three dimensional (3D) printing, is increasingly being used for personalized orthopedic implants. Additively manufactured components normally undergo further processing, in particular 3D printed locking osteosynthesis plates require post‐printing screw thread creation. The aim of this study was to compare 3D printed threads with machined and hand‐tapped threads for a locking plate application. Pushout tests were performed on 115 additively manufactured specimens with tapered screw holes; additive manufacture was performed at 0°, 20°, 45°, or 90° build orientations. The screw holes were either machined, hand‐tapped or 3D printed. The 3D printed screw holes were left as printed, or run through with a tap lubricated with water or with thread cutting oil. Printed threads run through using oil, with a build orientation of 90°, had comparable pushout force (median: 6377 N 95% confidence interval [CI]: 5616‐7739 N) to machined (median: 6757 N; 95% CI: 6682‐7303 N) and hand‐tapped (median: 7805 N; 95% CI: 7154‐7850 N) threads. As printed threads and those run through using water had significantly lower pushout forces. This study shows for the first time that 3D printed screw threads for a locking osteosynthesis plate application have comparable strength to traditionally produced screw threads.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.