Pyrolysis of straw pellets and wood strips was performed in a fixed bed reactor. The chars, solid products of thermal degradation, were used as potential materials for activated carbon production. Chemical and physical activation processes were used to compare properties of the products. The chemical activation agent KOH was chosen and the physical activation was conducted with steam and carbon dioxide as oxidising gases. The effect of the activation process on the surface area, pore volume, structure and composition of the biochar was examined. The samples with the highest surface area (1349.6 and 1194.4 m2/g for straw and wood activated carbons, respectively) were obtained when the chemical activation with KOH solution was applied. The sample with the highest surface area was used as an adsorbent for model wastewater contamination removal.
This article covers new application for char as a carrier of phase-change materials (PCM) that could be used as an additive to building materials. Being composed of bio-char and PCM, the granulate successfully competes with more expensive commercial materials of this type, such as Micronal® PCM. As a PCM carrier, char that was obtained from the pyrolysis of chestnut fruit (Aesculus hippocastanum) with different absorbances of the model phase-change material, Rubitherm RT22, was tested. DSC analysis elucidated several thermal properties (such as enthalpy, phase transition temperature, and temperature peak) of those mixtures and the results were compared with a commercial equivalent, Micronal DS 5040 X. Comparative research, approximating realistic conditions, were also performed by cooling and heating samples in a form of coatings that were made from chars with different content of RT22. These results indicated that the use of char as a PCM carrier was not only possible, but also beneficial from a thermodynamic point of view and it could serve as an alternative to commercial products. In this case, adsorption RT22 into char allowed for temperature stabilization comparable to Micronal DS 5040 X with ease of use as well as the economic advantages of being very low cost to produce due to microencapsulation. Other advantage of the proposed solution is related with the application of char obtained from waste biomass pyrolysis as a PCM carrier, and using this product in building construction to improve thermal comfort and increase energy efficiency.
The aim of this study was to assess the possibility of using furniture waste for smokeless fuel production using the pyrolysis process. Four types of wood-based wastes were used in the pyrolysis process: pine sawdust (PS), chipboard (CB), medium-density fiberboard (MDF), and oriented strand board (OSB). Additionally, the slow and fast types of pyrolysis were compared, where the heating rates were 15 °C/min and 100 °C/min, respectively. Chemical analyses of the raw materials and the pyrolysis product yields are presented. A significant calorific value rise was observed for the solid pyrolysis products (from approximately 17.5 MJ/kg for raw materials up to approximately 29 MJ/kg for slow pyrolysis products and 31 MJ/kg for fast pyrolysis products). A higher carbon content of char was observed in raw materials (from approximately 48% for raw materials up to approximately 75% for slow pyrolysis products and approximately 82% for fast pyrolysis products) than after the pyrolysis process. This work presents the possibility of utilizing waste furniture material that is mostly composed of wood, but is not commonly used as a substrate for conversion into low-emission fuel. The results prove that the proposed solution produced char characterized by the appropriate properties to be classified as smokeless coal.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.