Polyelectrolyte adsorption onto an oppositely charged interface is determined by electrostatic and secondary interactions. Since polyelectrolytes precipitate at elevated temperatures, the secondary interactions are presumably temperature dependent. This idea is tested for poly(allylamine) hydrochloride/ polystyrene sulfonate (PAH/PSS) films adsorbed from aqueous KCl solution (high salt conditions) at temperatures between 5 and 40 °C. KCl was chosen because the films were thicker than those obtained from NaCl or CsCl solutions indicating strong specific binding between K and PSS. The film thickness increases continuously with the adsorption temperature; the changes amount to 20-40%, depending on salt conditions. Furthermore, the roughness is increased, up to a factor of 5. The latter is attributed to the decreased percentage of strong electrostatic bonds within the polyelectrolyte multilayer. Another path to increased roughening is using low-weight polymers with a contour length similar to the thickness of a polycation/polyanion pair.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.