Continuous-wave operation of InGaN green laser diodes (LDs) on semipolar f2021g GaN substrates with output powers of over 100 mW in the spectral region beyond 530 nm is demonstrated. Wall plug efficiencies (WPEs) as high as 7.0-8.9% are realized in the wavelength range of 525-532 nm, which exceed those reported for c-plane LDs. The longest lasing wavelength has reached 536.6 nm under cw operation. These results suggest that the InGaN green LDs on the f20 21g plane are better suited as light sources for applications requiring wavelengths over 525 nm.

AlGaInN‐based blue–violet laser diodes with a single broad‐area stripe emitter were successfully fabricated on GaN substrates. Three stripe widths were examined; 10, 50, and 100 μm, and the maximum light output power of 0.94 W under cw operation at 20 °C was achieved for the sample with a stripe width of 10 μm. A super high‐power laser diode array was fabricated using 11 of these high‐performance laser chips, with a resultant output power of 6.1 W under cw operation at 20 °C. This result represents the highest reported output power for blue–violet laser diodes. (© 2003 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)

True green GaInN laser diodes with a lasing wavelength above 525 nm under continuous wave operation have been successfully fabricated on semipolar {2021} GaN substrates by improving both the diode structure and epitaxial growth conditions. At a case temperature of 55 °C, their lifetime was estimated to be over 5000 h for an optical output power of 50 mW and over 2000 h at 70 mW.

No abstract

No abstract