Sodium-ion batteries (SIBs) receive significant attention for electrochemical energy storage and conversion owing to their wide availability and the low cost of Na resources. However, SIBs face challenges of low specific energy, short cycling life, and insufficient specific power, owing to the heavy mass and large radius of Na(+) ions. As an important component of SIBs, cathode materials have a significant effect on the SIB electrochemical performance. The most recent advances and prospects of inorganic and organic cathode materials are summarized here. Among current cathode materials, layered transition-metal oxides achieve high specific energies around 600 mW h g(-1) owing to their high specific capacities of 180-220 mA h g(-1) and their moderate operating potentials of 2.7-3.2 V (vs Na(+) /Na). Porous Na3 V2 (PO4 )3 /C nanomaterials exhibit excellent cycling performance with almost 100% retention over 1000 cycles owing to their robust structural framework. Recent emerging cathode materials, such as amorphous NaFePO4 and pteridine derivatives show interesting electrochemical properties and attractive prospects for application in SIBs. Future work should focus on strategies to enhance the overall performance of cathode materials in terms of specific energy, cycling life, and rate capability with cationic doping, anionic substitution, morphology fabrication, and electrolyte matching.

MoS2 nanoflowers with expanded interlayer spacing of the (002) plane were synthesized and used as high-performance anode in Na-ion batteries. By controlling the cut-off voltage to the range of 0.4-3 V, an intercalation mechanism rather than a conversion reaction is taking place. The MoS2 nanoflower electrode shows high discharge capacities of 350 mAh g(-1) at 0.05 A g(-1) , 300 mAh g(-1) at 1 A g(-1) , and 195 mAh g(-1) at 10 A g(-1) . An initial capacity increase with cycling is caused by peeling off MoS2 layers, which produces more active sites for Na(+) storage. The stripping of MoS2 layers occurring in charge/discharge cycling contributes to the enhanced kinetics and low energy barrier for the intercalation of Na(+) ions. The electrochemical reaction is mainly controlled by the capacitive process, which facilitates the high-rate capability. Therefore, MoS2 nanoflowers with expanded interlayers hold promise for rechargeable Na-ion batteries.

High-performance rechargeable Na/FeS2batteries showing only the intercalation reaction are obtained by selecting a NaSO3CF3/diglyme electrolyte and tuning the cut-off voltage to 0.8 V.