Pure soluble silica prepared by a sol-gel method induced bone-like hydroxyapatite formation onto its surface when the silica was immersed in a simulated body fluid (SBF), whereas silica glass and quartz did not. This finding directly supports the hypothesis that hydrated silica plays an important role in biologically active hydroxyapatite formation on the surfaces of bioactive glasses and glass-ceramics, which leads to bone-bonding. Gel-derived titania is also a hydroxyapatite inducer because of its abundant TiOH groups. These results provide further insight into the unique osseointegration of titanium and its alloys. It is suspected that gel-derived titania develops an apatite layer by taking calcium and phosphate from the body fluid, thus producing bone-bonding. Although sufficient AlOH groups may remain in the alumina gel, they do not serve to initiate apatite generation when immersed in SBF. This phenomenon explains the fact that an intermediate fibrous tissue is usually found to separate the alumina implant from bone. One may infer that both abundant OH groups and negatively charged surfaces of gel-derived silica and titania are important for hydroxyapatite induction. material which possesses and/or develops both a negatively charged surface and abundant OH groups in a physiologically-related fluid is most likely to be an efficient apatite inducer. Such materials are suitable candidates to serve as bone-bonding biomaterials.
The need for bone tissue regeneration is continuously expanding due to the improvement of life quality and the consequent increase in life expectancy. Although natural bone grafts have shown excellent clinical successes, their use is associated with some important drawbacks, limited availability being one of the most important. Cell- and growth-factor based tissue engineering provides a promising alternative to natural bone grafts; however, the performance of tissue-engineered constructs often depends on the used carrier. An important challenge in the field of bone regeneration is the development of synthetic bone graft substitutes that are "intelligent" in that they are able to instruct the in vivo environment to form bone. A group of potentially "intelligent" bone graft substitutes are osteoinductive biomaterials. In this paper, background on the phenomenon of osteoinduction and an overview of synthetic biomaterials with osteoinductive potential are given. Furthermore, we elaborate on physicochemical properties of biomaterials that are of influence on their osteoinductive potential. Finally, we discuss the relevance of osteoinductivity of biomaterials in the repair of clinically relevant bone defects.
The combination of the high mechanical strength of metals with the osteoconductive properties of calcium phosphates make hydroxyapatite coatings on titanium implants widely used in orthopedic surgery. However, the most popular coating method, plasma spraying, exhibits some important drawbacks: the inability to cover porous implants and to incorporate biologically active agents, delamination, and particle release. The aim of this study was to elaborate a dense, strong, and thick calcium-phosphate coating on titanium and poroustantalum implants using a two-step biomimetic procedure. In the first step, the implants were soaked in a solution that was 5 times more concentrated than regular simulated body fluid (SBF-A solution). A thin but uniform amorphous calciumphosphate coating was deposited on the metal. Then, the implants were immersed in the SBF-B solution, which had a similar composition as the SBF-A solution, but with decreased contents of crystal growth inhibitors (i.e., Mg 2؉ and HCO 3 ؊ ). This resulted in the fast precipitation of a 30 m thick crystalline calcium-phosphate coating. The pH of the SBF-B solution and the thickness of the crystalline coating layer were studied as a function of time. The Fourier transform infrared spectra and X-ray diffraction patterns showed that this new coating closely resembles bone mineral. Our biomimetic coating should facilitate rapid bone formation around the implant, reducing therewith the patient's recovery time after surgery.
Different materials were implanted in muscles of dogs to study the osteoinduction of calcium phosphate biomaterials. Bone formation was only seen in calcium phosphate biomaterials with micropores, and could be found in hydroxyapatite (HA) ceramic, tricalcium phosphate/hydroxyapatite ceramic (BCP), beta-TCP ceramic and calcium phosphate cement. The osteoinductive potential was different in different materials. The results indicate that osteoinduction can be a property of calcium phosphate biomaterials when they exhibit specific chemical and structural characteristics.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.