The present work reports on the development of photo-cross-linkable gelatins sufficiently versatile to overcome current biopolymer two-photon polymerization (2PP) processing limitations. To this end, both the primary amines as well as the carboxylic acids of gelatin type B were functionalized with photo-cross-linkable moieties (up to 1 mmol/g) resulting in superior and tunable mechanical properties (G′ from 5000 to 147000 Pa) enabling efficient 2PP processing. The materials were characterized in depth prior to and after photoinduced cross-linking using fully functionalized gelatin-methacrylamide (gel-MOD) as a benchmark to assess the effect of functionalization on the protein properties, cross-linking efficiency, and mechanical properties. In addition, preliminary experiments on hydrogel films indicated excellent in vitro biocompatibility (close to 100% viability) both in the presence of MC3T3 preosteoblasts and L929 fibroblasts. Moreover, 2PP processing of the novel derivative was superior in terms of applied laser power (≥40 vs ≥60 mW for gel-MOD at 100 mm/s) as well as post-production swelling (0–20% vs 75–100% for gel-MOD) compared to those of gel-MOD. The reported novel gelatin derivative (gel-MOD-AEMA) proves to be extremely suitable for direct laser writing as both superior mimicry of the applied computer-aided design (CAD) was obtained while maintaining the desired cellular interactivity of the biopolymer. It can be anticipated that the present work will also be applicable to alternative biopolymers mimicking the extracellular environment such as collagen, elastin, and glycosaminoglycans, thereby expanding current material-related processing limitations in the tissue engineering field.
In the present work, gelatin type B is modified with highly reactive norbornene functionalities (Gel-NB) following a one-pot synthesis approach to enable subsequent thiol-ene photo-click crosslinking. The modification strategy displays close control over the amount of introduced functionalities. Additionally, Gel-NB exhibits considerably improved processing capabilities in terms of two-photon polymerization when benchmarked to earlier-reported crosslinkable gelatin derivatives (e.g., gelatin-methacrylamide (Gel-MOD) and gelatin-methacrylamide-aminoethylmethacrylate (Gel-MOD-AEMA)). The improvement is especially apparent in terms of minimally required laser power (20 mW vs ≥60 mW (Gel-MOD) vs ≥40 mW (Gel-MOD-AEMA) at 100 mm s scan speed) and processable concentration range (≥5 w/v% vs ≥10 w/v% (Gel-MOD/Gel-MOD-AEMA)). Furthermore, the proposed functionalization scheme maintains the excellent biocompatibility and cell interactivity of gelatin. Additionally, the norbornene functionalities have potential for straightforward postprocessing "thiol-ene" surface grafting of active molecules. As a consequence, a very promising material toward tissue engineering applications and more specifically, biofabrication, is presented.
Graphene is considered a record-performance nonlinear-optical material on the basis of numerous experiments. The observed strong nonlinear response ascribed to the refractive part of graphene’s electronic third-order susceptibility χ(3) cannot, however, be explained using the relatively modest χ(3) value theoretically predicted for the 2D material. Here we solve this long-standing paradox and demonstrate that, rather than χ(3)-based refraction, a complex phenomenon which we call saturable photoexcited-carrier refraction is at the heart of nonlinear-optical interactions in graphene such as self-phase modulation. Saturable photoexcited-carrier refraction is found to enable self-phase modulation of picosecond optical pulses with exponential-like bandwidth growth along graphene-covered waveguides. Our theory allows explanation of these extraordinary experimental results both qualitatively and quantitatively. It also supports the graphene nonlinearities measured in previous self-phase modulation and self-(de)focusing (Z-scan) experiments. This work signifies a paradigm shift in the understanding of 2D-material nonlinearities and finally enables their full exploitation in next-generation nonlinear-optical devices.
We experimentally demonstrate a negative Kerr nonlinearity for quasi-undoped graphene. Hereto, we introduce the method of chirped-pulse-pumped self-phase modulation and apply it to graphenecovered silicon waveguides at telecom wavelengths. The extracted Kerr-nonlinear index for graphene equals n2,gr = −10 −13 m 2 /W. Whereas the sign of n2,gr turns out to be negative in contrast to what has been assumed so far, its magnitude is in correspondence with that observed in earlier experiments. Graphene's negative Kerr nonlinearity strongly impacts how graphene should be exploited for enhancing the nonlinear response of photonic (integrated) devices exhibiting a positive nonlinearity. It also opens up the possibility of using graphene to annihilate unwanted nonlinear effects in such devices, to develop unexplored approaches for establishing Kerr processes, and to extend the scope of the "periodic poling" method often used for second-order nonlinearities towards third-order Kerr processes. Because of the generic nature of the chirped-pulse-pumped self-phase modulation method, it will allow fully characterizing the Kerr nonlinearity of essentially any novel (2D) material.
Photocrosslinkable gelatin hydrogels are excellent bioinks or biomaterial ink components to serve biofabrication applications. Especially the widely investigated gelatin-methacroyl (gel-MA) hydrogels hold an impressive track record. However, over the past decade, increasing attention is being paid to thiol-ene photo-click chemistry to obtain hydrogel networks benefitting from a faster reactivity (i.e. seconds vs minutes) along with superior biocompatibility and processability. In order to exploit this photo-click chemistry, often an ene-functionality (e.g. norbornene) is introduced onto gelatin followed by crosslinking in the presence of a multifunctional thiol (e.g. dithiothreitol). To date, very limited research has been performed on the influence of the applied thiolated crosslinker on the final hydrogel properties. Therefore, the present work assesses the influence of different thiolated crosslinkers on the crosslinking kinetics, mechanical properties and biological performance of the hydrogels upon encapsulation of primary adipose tissue-derived stem cells which indicated a cell viability exceeding 70%. Furthermore, the different formulations were processed using two-photon polymerization which indicated, in addition to differences in processing window and swelling ratio, a previously unreported phenomenon. At high intensities (i.e. ⩾150 mW), the laser results in cleavage of the gelatin backbone even in the absence of distinct photo-cleavable functionalities. This can have potential to introduce channels or softer regions in gels to result in zones characterized by different degradation speeds or the formation of blood vessels. Consequently, the present study can be used to provide guidance towards tailoring the thiol-ene system towards the desired applications.
The present work describes for the first time the production of self-supporting low gelatin density (<10 w/v%) porous scaffolds using methacrylamide-modified gelatin as an extracellular matrix mimicking component. As porous scaffolds starting from low gelatin concentrations cannot be realized with the conventional additive manufacturing techniques in the abscence of additives, we applied an indirect fused deposition modelling approach. To realize this, we have printed a sacrificial polyester scaffold which supported the hydrogel material during UV crosslinking, thereby preventing hydrogel structure collapse. After complete curing, the polyester scaffold was selectively dissolved leaving behind a porous, interconnective low density gelatin scaffold. Scaffold structural analysis indicated the success of the selected indirect additive manufacturing approach. Physico-chemical testing revealed scaffold properties (mechanical, degradation, swelling) to depend on the applied gelatin concentration and methacrylamide content. Preliminary biocompatibility studies revealed the cell-interactive and biocompatible properties of the materials developed.
Over the past decades, solid freeform fabrication (SFF) has emerged as the main technology for the production of scaffolds for tissue engineering applications as a result of the architectural versatility. However, certain limitations have also arisen, primarily associated with the available, rather limited range of materials suitable for processing. To overcome these limitations, several research groups have been exploring novel methodologies through which a construct, generated via SFF, is applied as a sacrificial mould for production of the final construct. The technique combines the benefits of SFF techniques in terms of controlled, patient-specific design with a large freedom in material selection associated with conventional scaffold production techniques. Consequently, well-defined 3D scaffolds can be generated in a straightforward manner from previously difficult to print and even "unprintable" materials due to thermomechanical properties that do not match the often strict temperature and pressure requirements for direct rapid prototyping. These include several biomaterials, thermally degradable materials, ceramics and composites. Since it can be combined with conventional pore forming techniques, indirect rapid prototyping (iRP) enables the creation of a hierarchical porosity in the final scaffold with micropores inside the struts. Consequently, scaffolds and implants for applications in both soft and hard tissue regeneration have been reported. In this review, an overview of different iRP strategies and materials are presented from the first reports of the approach at the turn of the century until now.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
334 Leonard St
Brooklyn, NY 11211
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.