Cu2SnS3 (CTS) contains non-rare metals and it has suitable optical characteristics for the absorber layer of thin-film solar cells. In this study, CTS thin films were fabricated by sulfurizing Cu–Sn precursors deposited by co-electrodeposition. Solar cells with a structure glass/Mo/CTS/CdS/ZnO:Al/Al were fabricated from the films. The best cell had an efficiency of 2.84%. A relatively high conversion efficiency was obtained from films with Cu/Sn≤2.

Cu2SnS3 (CTS) has been reported to have various band gap energies in the range of 0.93–1.77 eV and an absorption coefficient of 1.0×104 cm-1. It consists of elements that are inexpensive due to their abundance in Earth's crust. Consequently, CTS is expected to be utilized in the absorber layers of thin-film solar cells. In this study, Cu/Sn stacked-layer thin-film precursors were deposited on glass and glass/Mo substrates by electron beam evaporation. CTS thin films were fabricated by sulfurizing the precursors at temperatures of 450–580 °C for 2 h in an atmosphere of N2 and sulfur vapor. CTS films were estimated to have band gap energies of 0.96–1.00 eV by extrapolation. A solar cell fabricated using a CTS thin film sulfurized at 580 °C exhibited an open-circuit voltage of 211 mV, a short-circuit current of 28.0 mA/cm2, a fill factor of 0.43, and a conversion efficiency of 2.54%.