Bioactive glasses exhibit the unique ability of bone bonding, thus creating a stable interface by stimulating bone cells toward mechanisms of regeneration and self‐repair activated by ionic dissolution products. Therefore, 3D glass‐derived scaffolds can be considered ideal porous templates to be used in bone tissue engineering strategies and regenerative medicine. This review provides a comprehensive overview of all technological aspects relevant to the fabrication of bioactive glass scaffolds, including the fundamentals of materials processing, a summary of the conventional porogen, and template‐based methods and of recent additive manufacturing technologies, which are promising for large‐scale production of highly reproducible and reliable implants suitable for a wide range of clinical applications.

No abstract

Zirconia (ZrO2) is a bioinert, strong, and tough ceramic, while titania (TiO2) is bioactive but has poor mechanical properties. It is expected that ZrO2-TiO2 mixed ceramics incorporate the individual properties of both ceramics, so that this material would exhibit better biological properties. Thus, the objective of this study was to compare the biocompatibility properties of ZrO2-TiO2 mixed ceramics. Sintered ceramics pellets, obtained from powders of TiO2, ZrO2, and three different ZrO2-TiO2 mixed oxides were used. Roughnesses, X-ray diffraction, microstructure through SEM, hardness, and DRIFT characterizations were performed. For biocompatibility analysis cultured FMM1 fibroblasts were plated on the top of disks and counted in SEM micrographs 1 and 2 days later. Data were compared by ANOVA complemented by Tukey's test. All samples presented high densities and similar microstructure. The H2O content in the mixed ceramics was more evident than in pure ceramics. The number of fibroblasts attached to the disks increased significantly independently of the experimental group. The cell growth on the top of the ZrO2-TiO2 samples was similar and significantly higher than those of TiO2 and ZrO2 samples. Our in vitro experiments showed that the ZrO2-TiO2 sintered ceramics are biocompatible allowing faster cell growth than pure oxides ceramics. The improvement of hardness is proportional to the ZrO2 content. Thus, the ZrO2-TiO2 sintered ceramics could be considered as potential implant material.