The autogenous shrinkage is a phenomenon that occurs due to the appearance of tensile stresses in capillary pores. Inherent in the hydration process, not depending on external interference. In high strength concrete, autogenous shrinkage is most pronounced, due to the refinement of microstructure, the high cement content, presence of mineral addictions and low water/cement ratio, which interfere in the transport of water curing. In this context, Superabsorbent polymers (SAP) stand out for their ability to reduce or eliminate the autogenous shrinkage, because they absorb large amounts of water, which is subsequently released into the matrix, avoiding self-desiccation and the onset of tensile stresses (internal curing). However, studies show that SAP can reduce the mechanical strength, which can be compensated by addiction of Nano-silica (NS). In this paper, the effect of these additions in Time Zero (T 0 ) was evaluated. T 0 determines the time at which the material starts to behave as a solid, with the development of a rigid mineral skeleton to oppose the volumetric variations that occurs in the paste, which can lead to cracking, compromising esthetics, durability, and structures safety. The ultrasonic pulse velocity test performed the T 0 , which measures the velocity of propagation of an ultrasonic wave through the material and is taken as the time when a sudden change occurs at this velocity. Nine blends were made containing SAP and NS, where it was found that SAP addition increases the T 0 (up to 11%), while NS decrease its value (in 55%).
RESUMO: A mensuração do desempenho ambiental pela metodologia de Avaliação do Ciclo de Vida (ACV) possibilita a compreensão dos impactos ambientais nas etapas do processo de produção de uma edificação. Para facilitar esse processo pode ser utilizado o Building Information Modeling (BIM). Neste contexto, o presente trabalho consistiu no estudo e avaliação da aplicação do BIM na ACV de edificações a partir de um estudo de caso utilizando softwares que trabalham na plataforma BIM, o Autodesk Revit e o DesignBuilder. Foi possível estimar as emissões de CO2 na fase de pré-uso de uma edificação escolar. No entanto, notou-se problemas na questão da interoperabilidade quando o modelo é exportado do primeiro para o segundo software. A quantificação das emissões foi realizada ainda manualmente, para comparação com os resultados fornecidos pelo software. Os resultados mostraram que a quantificação de CO2 é mais precisa para sistemas construtivos homogêneos, como paredes de concreto. A principal contribuição do presente estudo foi a verificação da viabilidade do software DesignBuilder para a quantificação das emissões de CO2 no ciclo de vida das edificações, como uma ferramenta de projeto para edificações de baixo carbono.ABSTRACT: The measurement of environmental performance using Life Cycle Assessment (LCA) methodology enables comprehensive understanding of environmental impacts in all stages of the production process of a building. In order to facilitate this process can be used the Building Information Modeling (BIM). In this context, the present paper aims to study and evaluate the implementation of BIM in LCA of buildings from a case study using software that works on the BIM platform, Autodesk Revit and DesignBuilder. It was possible to estimate the CO2 emissions in the pre-use stage of a school building. However, problems have been noted in the interoperability issue when the model is exported from the first to the second software. The CO2 emission quantification was still performed manually, for comparison with the results provided by the software. The results showed that the quantification of CO2 is more accurate for homogeneous constructive systems, such as concrete walls The main contribution of the present study was the verification of the viability of the DesignBuilder software for the quantification of CO2 emissions in the life cycle of buildings, as a design tool for low carbon buildings.
RESUMO A aplicação da técnica de calorimetria por condução isotérmica possibilita a avaliação da velocidade das reações de hidratação de forma simplificada e eficiente, ao longo do tempo, pelas curvas de evolução de calor. Essa técnica pode ser a ferramenta adequada para a avaliação do processo de dessorção do polímero superabsorvente (SAP), parâmetro fundamental que determina a eficiência do polímero como agente mitigador da retração autógena. Com o uso da calorimetria foi possível avaliar o comportamento do SAP durante o estado fresco e a mudança que a nanosílica (NS) causou na cinética de hidratação dos compostos cimentícios. Nas pastas estudadas nesse trabalho, observou-se um leve retardo na ocorrência do pico principal de hidratação do C3S nas pastas contendo SAP e uma aceleração das reações de hidratação das pastas contendo NS. Notou-se ainda que quanto maior a quantidade de SAP e de NS, maior foi a quantidade de calor liberado, o que pode ser correlacionado com maior formação de hidratos.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.