In both continuous casting of steel slabs and direct chill (DC) casting of aluminum alloy ingots, water is used to cool the mold in the initial stages of solidification, and then below the mold, where it is in direct contact with the newly solidified surface of the metal. Water cooling affects the product quality by (1) controlling the heat removal rate that creates and cools the solid shell and (2) generating thermal stresses and strains inside the solidified metal. This work reviews the current stateof-the-art in water cooling for both processes, and draws insights by comparing and contrasting the different practices used in each process. The heat extraction coefficient during secondary cooling depends greatly on the surface temperature of the ingot, as represented by boiling water-cooling curves. Thus, the heat extraction rate varies dramatically with time, as the slab/ingot surface temperature changes. Sudden fluctuations in the temperature gradients within the solidifying metal cause thermal stresses, which often lead to cracks, especially near the solidification front, where even small tensile stresses can form hot tears. Hence, a tight control of spray cooling for steel, and practices such as CO 2 injection/pulse water cooling for aluminum, are now used to avoid sudden changes in the strand surface temperature. The goal in each process is to match the rate of heat removal at the surface with the internal supply of latent and sensible heat, in order to lower the metal surface temperature monotonically, until cooling is complete.
Surface velocity of the molten steel in the mold is critical to final product quality during continuous casting of steel, and is one of the few flow parameters that can be measured in the plant to validate fluid flow models. Surface velocity was measured using two different sensors: Sub-meniscus Velocity Control (SVC) devices and nail dipping, to evaluate their performance, and to quantify surface velocities in a commercial steel caster under different casting speeds, argon gas fractions, and mold widths. A correlation between the height difference of the solidified lump on the nail and surface velocity is confirmed and extended. Reasonable agreement between the two sensing methods was obtained, both in trends and magnitudes for both time-averaged velocity and transient flows. Transient CFD models are applied to simulate multiphase flow of steel and gas bubbles in the Submerged Entry Nozzle (SEN) and mold and are validated with nail dipping measurements. To obtain the transient inlet boundary conditions for the simulation, two semi-empirical models, a stopper-position-based model and a metal-level-based model, predict the liquid steel flow rate through the SEN based on recorded plant data. The model system was applied to study the effects of stopper rod movements on transient flow in the SEN and mold. Mold level fluctuations were calculated using a simple pressure method and compared with plant measurements. The results show that severe stopper rod movements cause significant disturbances of the meniscus level, which may cause slag entrapment, leading to sliver defects in the final product.
The flow of melted mold powder into the interfacial gap between the strand and the mold wall is important for productivity and quality in continuous cast slabs. Some of the mold slag (flux) consumption provides true lubrication, while much of the rest is trapped in the oscillation marks on the slab surface. This work presents measurements of powder consumption from extensive careful plant trials on ultra-low carbon steels, and a new, simple, semi-empirical model to predict slag consumption. The model predicts "lubrication consumption" by deducting the slag carried in the oscillation marks from the measured total. The oscillation mark shape is estimated from a theoretical analysis of equilibrium meniscus shape, which is based on metallographic analysis of many hook and oscillation mark shapes. The model demonstrates that the fraction consumed in the oscillation marks decreases with increasing casting speed, because the oscillation mark depth depends more on casting speed than on mold oscillation conditions. The model is validated by successful prediction of known trends of oscillation mark depth and mold powder consumption with changing various operation parameters. The model provides new insight into mold lubrication phenomena, which is important for extending casting operation to higher speeds and new lubrication regimes.KEY WORDS: continuous casting; mold powder; slag; flux; lubrication; oscillation marks; mold oscillation; stroke; frequency; modification ratio; negative strip time; positive strip time; casting speed; meniscus; models; plant experiments.ISIJ International, Vol. 46 (2006), No. 11, pp. 1635No. 11, pp. -1644 slag as shown in Fig. 1(a). The solid slag layers are glassy, crystalline, or mixtures of both 14) depending on the slag composition and local cooling rate history. [15][16][17] Several previous models of heat transfer and lubrication assume that the gap has a uniform thickness. [18][19][20] However, the real strand surface contains periodic transverse depressions called oscillation marks (OM) in Fig. 1(b). The volume of these depressions generally consumes a significant amount of slag, which greatly affects lubrication and leads to nonuniform heat transfer in the mold. 21) Thus, quantifying the oscillation mark shape is a necessary prerequisite for the prediction of lubrication and heat transfer in the mold.In this study, mold powder consumption was measured during casting trials conducted at POSCO Gwangyang Works for several different oscillation conditions and casting speeds. The measured consumptions were divided into two components: 1) the slag entrapped in the oscillation marks and 2) the remaining flux, which provides lubrication to prevent sticking, as shown in Fig. 1(b). This "lubrication consumption" is a more realistic concept to represent lubrication than total mold powder consumption.17) The oscillation mark shape is calculated by combining measured OM depths with a realistic profile based on fundamentals. 22) Correlations are found for OM depth, corresponding OM consumption, l...
The initial stages of solidification near the meniscus during continuous casting of steel slabs involve many complex inter-related transient phenomena, which cause periodic oscillation marks (OMs), subsurface hooks, and related surface defects. This article presents a detailed mechanism for the formation of curved hooks and their associated OMs, based on a careful analysis of numerous specially etched samples from ultra-low-carbon steel slabs combined with previous measurements, observations, and theoretical modeling results. It is demonstrated that hooks form by solidification and dendritic growth at the liquid meniscus during the negative strip time. Oscillation marks form when molten steel overflows over the curved hook and solidifies by nucleation of undercooled liquid. The mechanism has been justified by its explanation of several plant observations, including the variability of hook and OM characteristics under different casting conditions, and the relationships with mold powder consumption and negative/positive strip times.
The control of the heat transfer during the start-up phase of the direct-chill (DC) casting process for aluminum sheet ingots is critical from the standpoint of defect formation. Process control is difficult because of the various inter-related phenomena occurring during the cast start-up. First, the transport of heat to the mold is altered as the ingot base deforms and the sides are pulled inward during the start-up phase. Second, the range of temperatures and water flow conditions occurring on the ingot surface as it emerges from the mold results in the full range of boiling-water heat-transfer conditions-e.g., film boiling, transition boiling, nucleate boiling, and convection-making the rate of transport highly variable. For example, points on the ingot surface below the point of water impingement can experience film boiling, resulting in the water being ejected from the surface, causing a dramatic decrease in heat transfer below the point of ejection. Finally, the water flowing down the ingot sides may enter the gap formed between the ingot base and the bottom block due to butt curl. This process alters the heat transfer from the base of the ingot and, in turn, affects the surface temperature on the ingot faces, due to the transport of heat within the ingot in the vertical direction. A comprehensive mathematical model has been developed to describe heat transfer during the start-up phase of the DC casting process. The model, based on the commercial finite-element package ABAQUS, includes primary cooling via the mold, secondary cooling via the chill water, and ingot-base cooling. The algorithm used to account for secondary cooling to the water includes boiling curves that are a function of ingot-surface temperature, water flow rate, impingement-point temperature, and position relative to the point of water impingement. In addition, a secondary cooling algorithm accounts for water ejection, which can occur at low water flow rates (low heat-extraction rates). The algorithm used to describe ingot-base cooling includes both the drop in contact heat transfer due to gap formation between the ingot base and bottom block (arising from butt curl) as well as the increase in heat transfer due to water incursion within the gap. The model has been validated against temperature measurements obtained from two 711 ϫ 1680 mm AA5182 ingots, cast under different start-up conditions (nontypical "cold" practice and nontypical "hot" practice). Temperature measurements were taken at various locations on the ingot rolling and narrow faces, ingot base, and top surface of the bottom block. Ingot-base deflection data were also obtained for the two test conditions. Comparison of the model predictions with the data collected from the cast/embedded thermocouples indicates that the model accounts for the processes of water ejection and water incursion and is capable of describing the flow of heat in the early stages of the casting process satisfactorily.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.