We report the fabrication, characterization, and modeling of photoconductive antennas (PCAs) using 40 nm thin-film flakes of black phosphorus (BP) as the photoconductor and hexagonal boron nitride (hBN) as a capping layer to prevent oxidation of BP. Dipole antennas were fabricated on oxidized high-resistivity Si substrates, and BP and hBN flakes were picked up and transferred onto the antenna inside a nitrogen glovebox. The transfer matrix technique was used to optimize the thickness of BP and hBN for maximum absorption. BP flakes were aligned with the armchair axis along the anode–cathode gap of the antenna, with crystal orientation measured using reflection anisotropy. Photocurrent imaging under illumination with 100 fs pulses at 780 and 1560 nm showed a bias-dependent maximum photocurrent localized to the antenna gap with a peak photoconductivity of 1 (2) S/cm in the linear regime of bias for excitation at 780 (1560) nm. Photocurrent saturation in bias (pump fluence) occurred at approximately 1 V (0.25mJ/cm2). Device performance was modeled numerically by solving Maxwell’s equations and the drift–diffusion equation to obtain the photocurrent density in response to pulsed laser excitation, which was largely in qualitative agreement with the experimental observations. THz output computed from surface current density suggests that BP THz PCA performance is at least comparable to more traditional devices based on low-temperature-grown GaAs. These devices represent a step toward high-performance THz photoconductive antennas using BP.

Epitaxial Al-InAs heterostructures appear as a promising materials platform for exploring mesoscopic and topological superconductivity. A unique property of Josephson junction field effect transistors (JJ-FETs) fabricated on these heterostructures is the ability to tune the supercurrent using a metallic gate. Here, we report the fabrication and measurement of gate-tunable Al-InAs JJ-FETs in which the gate dielectric in contact with the InAs is produced by mechanically exfoliated hexagonal boron nitride (h-BN) followed by dry transfer. We discuss a versatile fabrication process that enables compatibility between layered material transfer and Al-InAs heterostructures that allows us to achieve full gate-tunability of supercurrent by using only 5 nm thick h-BN flakes. Our study shows that pristine properties of epitaxial Josephson junctions, such as product of normal resistance and critical current, I c R n, are preserved. Furthermore, complementary measurements confirm that using h-BN dielectric changes the channel density less when compared to atomic layer deposition of Al2O3.

We describe methods for producing and analyzing large, thin flakes of air-sensitive two-dimensional materials. Thin flakes of layered or van der Waals crystals are produced using mechanical exfoliation, in which layers are peeled off a bulk crystal using adhesive tape. This method produces high-quality flakes, but they are often small and can be hard to find, particularly for materials with relatively high cleavage energies such as black phosphorus. By heating the substrate and the tape, two-dimensional material adhesion to the substrate is promoted, and the flake yield can be increased by up to a factor of ten. After exfoliation, it is necessary to image or otherwise analyze these flakes but some twodimensional materials are sensitive to oxygen or water and will degrade when exposed air. We have designed and tested a hermetic transfer cell to temporarily maintain the inert environment of a glovebox so that air-sensitive flakes can be imaged and analyzed with minimal degradation. The compact design of the transfer cell is such that optical analysis of sensitive materials can be performed outside of a glovebox without specialized equipment or modifications to existing equipment.

We describe methods for producing and analyzing large, thin flakes of air-sensitive two-dimensional materials. Thin flakes of layered or van der Waals crystals are produced using mechanical exfoliation, in which layers are peeled off a bulk crystal using adhesive tape. This method produces high-quality flakes, but they are often small and can be hard to find, particularly for materials with relatively high cleavage energies such as black phosphorus. By heating the substrate and the tape, two-dimensional material adhesion to the substrate is promoted, and the flake yield can be increased by up to a factor of ten. After exfoliation, it is necessary to image or otherwise analyze these flakes but some twodimensional materials are sensitive to oxygen or water and will degrade when exposed air. We have designed and tested a hermetic transfer cell to temporarily maintain the inert environment of a glovebox so that air-sensitive flakes can be imaged and analyzed with minimal degradation. The compact design of the transfer cell is such that optical analysis of sensitive materials can be performed outside of a glovebox without specialized equipment or modifications to existing equipment.

We report the fabrication, characterization, and modeling of photoconductive antennas using 40 nm thin-film flakes of black phosphorus (BP) as the photoconductor and hexagonal boron nitride (hBN) as a capping layer to prevent oxidation of BP. Dipole antennas were fabricated on oxidized high-resistivity Si substrates, and BP and hBN flakes were picked up and transferred onto the antenna inside a nitrogen glovebox. The transfer matrix technique was used to optimize the thickness of BP and hBN for maximum absorption. BP flakes were aligned with the armchair axis along the anode-cathode gap of the antenna, with crystal orientation measured using reflection anisotropy. Photocurrent imaging under illumination with 100 fs pulses at 780 and 1560 nm showed a bias-dependent maximum photocurrent localized to the antenna gap with a peak photoconductivity of 1 (2) S/cm in the linear regime of bias for excitation at 780 (1560) nm. Photocurrent saturation in bias (pump fluence) occurred at approximately 1 V (0.25 mJ/cm 2 ). Device performance was modeled numerically by solving Maxwell's equations and the drift-diffusion equation to obtain the photocurrent density in response to pulsed laser excitation, which was largely in qualitative agreement with the experimental observations. THz output computed from surface current density suggests that BP THz PCA performance is at least comparable to more traditional devices based on low-temperature-grown GaAs. These devices represent a step toward high-performance THz photoconductive antennas using BP.