No abstract

No abstract

We have synthesized Pb(Zr0.52Ti0.48)O3 fibres with diameters ranging from 500 nm to several microns using electrospinning and metallo-organic decomposition techniques (Wang et al 2002 Mater. Res. Soc. Symp. Proc. 702 359). By a refinement of our electrospinning technique, i.e. by increasing the viscosity of the precursor solution, and by adding a filter to the tip of the syringe, the diameter of the synthesized PZT fibres has been reduced to the neighbourhood of 100 nm. The complex thermal decomposition was characterized using Fourier-transform infrared (FTIR) spectroscopy and x-ray diffraction (XRD). It was found that alcohol evaporated during electrospinning and that most of the organic groups had pyrolysed before the intermediate pyrochlore phase was formed. There is a good correspondence between XRD and FTIR spectra. We also verify that a thin film of platinum coated on the silicon substrate catalyses the phase transformation of the pyrochlore into the perovskite phase.

No abstract

Carbon nanofibers were produced from polyacrylonitrile/N, N-Dimethyl Formamide (PAN/DMF) precursor solution using electrospinning and vacuum pyrolysis at temperatures from 773-1273 K for 0.5, 2, and 5 h, respectively. Their conductance was determined from I -V curves. The length and cross-section area of the nanofibers were evaluated using optical microscope and scanning probe microscopes, respectively, and were used for their electrical conductivity calculation. It was found that the conductivity increases sharply with the pyrolysis temperature, and increases considerably with pyrolysis time at the lower pyrolysis temperatures of 873, 973, and 1073 K, but varies, less obviously, with pyrolysis time at the higher pyrolysis temperatures of 1173 and 1273 K. This dependence was attributed to the thermally activated transformation of disordered to graphitic carbons. KeywordsCarbon, conductivity measurement, electrostatic processes, nanotechnology This material is posted here with permission of the IEEE. Such permission of the IEEE does not in any way imply IEEE endorsement of any of the University of Pennsylvania's products or services. Internal or personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution must be obtained from the IEEE by writing to pubs-permissions@ieee.org. By choosing to view this document, you agree to all provisions of the copyright laws protecting it. Abstract-Carbon nanofibers were produced from polyacrylonitrile/N, N-Dimethyl Formamide (PAN/DMF) precursor solution using electrospinning and vacuum pyrolysis at temperatures from 773-1273 K for 0.5, 2, and 5 h, respectively. Their conductance was determined from -curves. The length and cross-section area of the nanofibers were evaluated using optical microscope and scanning probe microscopes, respectively, and were used for their electrical conductivity calculation. It was found that the conductivity increases sharply with the pyrolysis temperature, and increases considerably with pyrolysis time at the lower pyrolysis temperatures of 873, 973, and 1073 K, but varies, less obviously, with pyrolysis time at the higher pyrolysis temperatures of 1173 and 1273 K. This dependence was attributed to the thermally activated transformation of disordered to graphitic carbons.