Cellulose scaffolds containing nano- or micro-hydroxyapatite (nHA or μHA) were prepared by the regeneration of cellulose from its acetylated derivative and the mechanical immobilization of inorganic particles, followed by freeze-drying. Microtomographic (micro-computed tomography) evaluation revealed that both scaffolds presented a highly interconnected porous structure, with a mean pore diameter of 490 ± 94 and 540 ± 132 μm for cellulose/nHA and cellulose/μHA, respectively. In vitro and in vivo characterizations of the developed scaffolds were investigated. Commercially available bone allograft was used as a control material. For the in vitro characterization, osteoblastic cell cultures were used and characterized over time to evaluate cell adhesion, metabolic activity, and functional output (alkaline phosphatase activity and osteoblastic gene expression). The results revealed greater spreading cell distribution alongside an increased number of filopodia, higher MTT values, and significantly increased expression of osteoblastic genes (Runx-2, alkaline phosphatase, and BMP-2) for cellulose/nHA, compared with cellulose/μHA and the control. The in vivo biocompatibility was evaluated in a rabbit calvarial defect model. The investigated scaffolds were implanted in circular rabbit calvaria defects. Four- and 12-week bone biopsies were investigated using micro-computed tomography and histological analysis. Although both cellulose/HA scaffolds outperformed the assayed control, a significantly higher amount of newly formed mineralized tissue was found within the defects loaded with cellulose/nHA. Within the limitations of this study, the developed cellulose/HA scaffolds showed promising results for bone regeneration applications. The biological response to the scaffold seems to be greatly dependent on the HA particles' characteristics, with cellulose scaffolds loaded with nHA eliciting an enhanced bone response.

No abstract

The aim of this study is to investigate the biomimetic mineralization on a cellulose-based porous matrix with an improved biological profile. The cellulose matrix was precalcified using three methods: (i) cellulose samples were treated with a solution of calcium chloride and diammonium hydrogen phosphate; (ii) the carboxymethylated cellulose matrix was stored in a saturated calcium hydroxide solution; (iii) the cellulose matrix was mixed with a calcium silicate solution in order to introduce silanol groups and to combine them with calcium ions. All the methods resulted in a mineralization of the cellulose surfaces after immersion in a simulated body fluid solution. Over a period of 14 days, the matrix was completely covered with hydroxyapatite crystals. Hydroxyapatite formation depended on functional groups on the matrix surface as well as on the precalcification method. The largest hydroxyapatite crystals were obtained on the carboxymethylated cellulose matrix treated with calcium hydroxide solution. The porous cellulose matrix was not cytotoxic, allowing the adhesion and proliferation of human osteoblastic cells. Comparatively, improved cell adhesion and growth rate were achieved on the mineralized cellulose matrices.

No abstract

No abstract