Eight nonstandardized gutta-percha points commercially available in Brazil (Konne, Tanari, Endopoint, Odous, Dentsply 0.04, Dentsply 0.06, Dentsply TP and Dentsply FM) were analysed chemically and by X-ray diffraction, and their chemical compositions were compared. The organic fraction (gutta-percha polymer and wax/resin) of the gutta-percha points was separated from the inorganic fraction (ZnO and BaSO4) by dissolving them in chloroform. The gutta-percha polymer was precipitated with acetone. The inorganic fraction was analysed by elemental microanalysis. Energy-dispersive X-ray microanalysis (EDX) and X-ray diffraction were employed to identify the chemical elements and compounds (barium sulfate and zinc oxide). The barium sulfate content was calculated based on the percentage of sulfur found in the elemental microanalysis. All analyses were repeated three times. The means and standard deviations of the percentage by weight of gutta-percha in the points were: Konne (17.6 +/- 0.30), Tanari (15.2 +/- 0.30), Endopoint (16.7 +/- 0.23), Odous (18.8 +/- 0.20), Dentsply 0.04 (15.7 +/- 0.17), Dentsply 0.06 (16.6 +/- 0.17), Dentsply TP (21.6 +/- 0.15) and Dentsply FM (16.3 +/- 0.23). The means and standard deviations of the zinc oxide content were: Konne (79.9 +/- 0.10), Tanari (81.9 +/- 0.07), Endopoint (81.3 +/- 0.40), Odous (79.7 +/- 0.26), Dentsply 0.04 (77.9 +/- 0.03), Dentsply 0.06 (78.2 +/- 0.07), Dentsply TP (69.8 +/- 0.19) and Dentsply FM (72.6 +/- 0.70). The method utilized was appropriate to quantify gutta-percha, wax/resin, zinc oxide and barium sulfate. Cone brands without barium sulfate were found. An unusual high wax/resin percentage was detected in Dentsply FM (p = 0.0003). Dentsply TP showed the highest gutta-percha percentage.
This study was undertaken to explore the effect of heating on gutta-percha, analyzing the occurrence of endothermic peaks corresponding to the transformation that occurs in the crystalline structure of the polymer during thermal manipulation. This study also sought to determine the temperature at which these peaks occur, causing a transformation from the beta- to the alpha-form, and from the alpha- to the amorphous phase. Eight nonstandardized gutta-percha points commercially available in Brazil (Konne, Tanari, Endopoint, Odous, Dentsply 0.04, Dentsply 0.06, Dentsply TP, Dentsply FM) and pure gutta-percha (control) were analysed using differential scanning calorimetry (DSC) and thermogravimetry analysis (TGA). The transition temperatures were determined and analysed. With the exception of Dentsply 0.04 and Dentsply 0.06, the majority of the products showed thermal behaviour typical of beta-gutta-percha, with two endothermic peaks, exhibiting two crystalline transformations upon heating from ambient temperature to 130 degrees. Upon cooling and reheating, few samples presented two endothermic peaks. It was concluded that heating dental gutta-percha to 130 degrees C causes changes to its chemical structure which permanently alter its physical properties.
This in vivo study investigated the time of degradation of root filling material (trans 1,4-polyisoprene) retrieved from endodontically treated teeth and correlated the occurrence of degradation with the longevity of endodontics. Thirty-six root-filled teeth with different filling times (2 to 30 years) and with and without periapical lesions were selected. All teeth presented clinical indication for root canal retreatment. The association among filling time, presence of periapical lesion and root filling material degradation was investigated. Root filling samples were retrieved from the root canals using a Hedström file without solvent. The trans 1,4-polyisoprene was isolated by root filling solubilization in chloroform followed by filtration and centrifugation. GPC and FT-IR were the analytical techniques utilized. Degradation of trans 1,4-polyisoprene occurred with time, as a slow process. It is an oxidative process, and production of carboxyl and hydroxyl groups in the residual polymer were observed. Statistically significant decrease of molar mass was observed after 5 (p=0.0001) and 15 (p=0.01) years in teeth with and without periapical lesion, respectively. Bacteria participated in polymer degradation. Gutta-percha aging was proven an important factor for the long-term success of endodontic treatment. The findings of the present study showed that, after 15 years, polymer weight loss may decrease the capacity of the filling mass to seal the root canal space and prevent re-infection, thus compromising significantly the longevity of root canal therapy.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.