Herein, a “nanonetwork” modified electrode was fabricated based on multiwalled carbon nanotubes and CeO2 nanorods. Scanning electron microscopy, X-ray powder diffraction and zeta potential were employed to characterize this electrode. Multiwalled carbon nanotubes negatively charged and CeO2 nanorods positively charged form “nanonetwork” via electrostatic interaction. The performance of the CeO2 nanorods-based electrode remarkably improved due to the introduction of multiwalled carbon nanotubes. The detection of rifampicin (RIF) was used as a model system to probe this novel electrode. The results showed a significant electrocatalytic activity for the redox reaction of RIF. Differential pulse voltammetry was used to detect rifampicin, the reduction peak current of rifampicin linear with the logarithm of their concentrations in the range of 1.0 × 10−13–1.0 × 10−6 mol/L, The linear equation is ip = 6.72 + 0. 46lgc, the detect limit is 3.4 × 10−14 mol/L (S/N = 3). Additionally, the modified electrode exhibits enduring stability, excellent reproducibility, and high selectivity. This strategy can be successfully used to detect trace rifampicin in samples with satisfactory results.
In an effort to expand the composition range over which A13Ti is stable, various amounts of niobium were substituted for titanium and processed by melt-spinning. Several samples were annealed both at 600'C and 1000°C for 24 hours. The effects of processing parameters such as wheel speed, the amount of niobium, and annealing temperatures on the structure were investigated by XRD and EXAFS. XRD showed that for all the samples the only structure present was D022. The D022 structure was stable even after the high temperature heat treatments. By means of EXAFS, niobium atoms were observed to occupy titanium sites in the D022 structure. Furthermore, in the unannealed samples, increasing wheel speed of the melt spinning process or the niobium concentration tended to distort the crystal structure. It was observed that Ti EXAFS had different results from the Nb EXAFS beyond their occupying similar sites, which suggested there may exist some composition zones, i.e. rich Nb zone or rich Ti zones, although the structures present were still D022. The samples were found to experience different distortions as a function of annealing temperatures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.