A gate stack structure consisting of a polycrystalline silicon germanium (poly-SiGe) conductor and a HfO2 dielectric on a silicon substrate was formed by inductively coupled plasma etching using HBr/Cl2/O2. Etch rates of poly-SiGe with 46% Ge were 1.7–2.0 times higher than those of polycrystalline silicon, depending on processing conditions. In the small feature sized devices of 100 nm gates, the notching at the sidewall of poly-SiGe was pronounced up to the depth of 50 nm. The amount of notching increased with increasing inductive power and pressure, and decreasing rf bias power. A HfO2 etch rate of 950 Å/min was obtained at the condition of 550 W inductive power, 360 W rf bias power, and 10 mTorr pressure. Etch rates of HfO2 increased with increasing inductive power and rf bias power. Etching selectivity of poly-SiGe with respect to HfO2 increased significantly with the addition of 3.8% O2 to HBr, and it was possible to control the selectivity in the range of 15–70 by changing the rf bias power. The change in etching selectivity was considered mainly due to the change in HfO2 film property, originating from the incorporation of O into the remaining nonvolatile Hf and the reformation of HfOx during etching.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.