The Mg-Zn-Y alloy containing the LPSO phase has excellent mechanical properties and functional application prospects. In an effort to clarify the electrically assisted deformation behavior of the Mg-Zn-Y alloy, electrically assisted tensile tests of Mg98.5Zn0.5Y1 alloy sheets were carried out at different temperatures, current densities, duty ratios, and frequencies. The experimental results showed that, after the pulse current was applied (26.58 A·mm−2), the peak stress of the sample deformed at 200 °C decreased by 8 MPa. The peak stress of the material decreased with the increase in current density. It is noticeable that the changes in duty ratios and frequencies have a small effect on the peak stress and strain. When the current was applied, more recrystallized grains appeared in the alloy and the basal texture was weakened. According to the experimental results, the Arrhenius model was derived based on the Zener–Hollomon parameter. Owing to the appearance of the stacking fault structure (LPSO), the activation energy Q of the Mg98.5Zn0.5Y1 alloy was 389.41 KJ/mol, which is higher than conventional Mg alloys. Moreover, the constitutive equation of the electro plastic effect coupled with temperature and pulse current parameters was established by introducing electrically assisted characteristics. By comparing the experimental and predicted values, the established model can effectively predict the variation trend of flow stress under electrically assisted deformation. Moreover, the constitutive model was incorporated into the UHARD subroutine of ABAQUS software to study the deformation behavior of the Mg98.5Zn0.5Y1 alloy.
In the present work, the microstructure and mechanical properties of Ti-6Al-4V alloy during multidirectional isothermal forging (MDIF) were systematically investigated. The evolution of the microstructure and texture of Ti-6Al-4V alloy during MDIF was studied using TEM and electron backscattered diffraction (EBSD). The experiment results showed that the grain size decreased with the increase in cumulative strain, especially in the easy deformation zone. After four deformation cycles, a homogeneous equiaxed grained microstructure with an average grain size of 0.14 μm was achieved. The texture changes of the alloy were studied in detail. After one cycle of MDIF, the texture was mainly composed of (0002) [01 10], and the Euler angles were (8°, 30°, 30°). The density of texture decreased with the increase in loading cycle, but the dispersion of texture increased. After four cycles of MDIF, the non-basal texture (1010) <1102> texture was observed, and the Euler angles were (82°, 33°, 0°). The highest achieved mechanical properties for Ti-6Al-4V alloy in the MDIF condition were a yield strength 900 MPa, ultimate tensile strength of 921 MPa, and an elongation of 12.1% at room temperature. The increase in MDIF cycles improved the hardness of the alloy. The significant improvement in mechanical properties was attributed to the ultrafine-grained microstructure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.