Effects of yttrium and erbium additions on glass-forming ability (GFA), thermal stability and mechanical properties of glassy Zr 55 Al 10 Ni 5 Cu 30 alloy were studied. (Zr 0:55 Al 0:10 Ni 0:05 Cu 0:30 ) 100Àx RE x (RE = Y, Er and x ¼ 0; 0:5; 1; 2; 3; 5 at%) metallic glasses were formed by melt-spinning and copper mold casting. It was found that the addition of Y or Er greatly enhanced the glass-forming ability, thermal stability and mechanical properties of Zr 55 Al 10 Ni 5 Cu 30 alloy. The alloys containing 1-3 at% Er can be cast into glassy rods with a diameter of 15 mm, which is larger than the critical diameter (10 mm) of the base alloy in the present work. With the addition of 1 at% Y, supercooled liquid region ÁT x of the base alloy was extended from 89 to 102 K, compressive strength was increased from 1650 to 1800 MPa and plastic strain reached a value as high as 3.5%.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.