1,3,5-Benzenetriphosphonic acid, H6BTP, 1,3,5-[(HO)2OP]3C6H3, was reacted hydrothermally with copper salts in the absence and presence of 4,4'-bipyridine (bpy) and 4,4'-trimethlyenedipyridine (tbpy) in a 1:1 molar ratio leading to three new organic-inorganic hybrid frameworks. Compound 1, {Cu6[C6H3(PO3)3]2(H2O)8} x 5.5 H2O, has three different copper ions that are interconnected by the highly charged [1,3,5-(PO3)3C6H3]6- anionic moieties. These moieties self-assemble through tetra-copper units to give a cagelike motif with two benzene rings parallel to each other at a distance of 3.531 A which extend along the a axis and link with a grouping of four-coordinated copper units in the b axis direction to give the cross-linked layered structure. In compound 2, Cu{C6H3[PO(OH)O]2[PO(OH)2]}(C10H8N2), the copper ions are in square pyramidal geometries and are interconnected via chelating and bridging BTP ligands into layers which are further cross-linked by bpy ligands into a pillared layered architecture. Compound 3, {Cu2C6H3[PO(OH)O]2[PO3](C13H14N2)} x 3 H2O x 0.5 HCON(CH3)2, contains tetra-copper units that are linked by BTP ligands and further linked by tbpy linkers in the c axis direction to produce a large channel-sized 3D framework.

Two novel tris(tert-butoxy)siloxy complexes of Pt(II) and Pt(IV) were prepared in high yields, (cod)Pt[OSi(O t Bu)3]2 (1; 87%; cod = 1,5-cyclooctadiene) and Me3Pt(tmeda)[OSi(O t Bu)3] (2; 81%; tmeda = N,N,N′,N′-tetramethylethylenediamine). The structures of these compounds were determined by multinuclear NMR spectroscopy and by single-crystal X-ray analysis. The thermolytic chemistry of 1 and 2 in the solid state was studied by thermogravimetric analysis. The thermal decomposition of these complexes resulted in the formation of Pt metal, with the elimination of HOSi(O t Bu)3. Precursors 1 and 2 react with the surface Si−OH groups of mesoporous SBA15 silica to generate surface-supported Pt centers. The coordination environments of the supported Pt centers in these new materials, termed Pt(II)SBA15 and Pt(IV)SBA15, were investigated using Fourier-transform infrared spectroscopy, X-ray absorption near-edge spectroscopy, and extended X-ray absorption fine structure analysis. These materials were also characterized using N2 porosimetry, powder X-ray diffraction and transmission electron microscopy. Comparisons with the molecular precursors 1 and 2 revealed many similarities, and the results are indicative of isolated Pt(II) and Pt(IV) centers. In addition, isolated Pt centers proved to be robust in inert atmosphere to 150−200 °C, which is similar to the decomposition temperatures of 1 and 2.

Hydroaminations of norbornene with arylsulfonamides and weakly basic anilines were achieved using electrophilic Pt(II) bis(triflate) complexes of the type L2Pt(OTf)2 (L2 = (t)Bu2bpy, (t)BuC6H4N== C(CH3)C(CH3)==NC6H4(t)Bu, (C6H5)2PCH2CH2P(C6H5)2, (C6F5)2PCH2CH2P(C6F5)2, S-BINAP). Pseudo-first-order kinetics reveal little to no dependence of the reaction rate on the ancillary ligand. Mechanistic studies do not favor an olefin coordination mechanism but are instead consistent with a mechanism involving sulfonamide coordination and generation of an acidic proton that is transferred to the norbornene. It is postulated that the resulting norbornyl cation is then attacked by free sulfonamide, and loss of proton from this adduct completes the hydroamination. The platinum-sulfonamide complex readily undergoes deprotonation to give a mu-amido platinum-bridged dimer that was isolated from the reaction solution. These studies also involve use of Me3SiPh and Me3SnPh as non-nucleophilic proton traps. Cleavage of the Ph-E bonds was used to detect the acidic, catalytically active species.